Durepol® PBT A3 NTLA010 BT307
| Category: | PBT , Polybutylene Terephthalate |
| Manufacturer: | Petropol Industry and Trade of Polymers LTDA |
| Trademark: | Durepol® PBT |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ZxlikR_Durepol-PBT-A3-NTLA010-BT307.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PBT polyester high viscosity. Ideal for injection molding. |
| General Information | |
|---|---|
| Features |
|
| Processing Method |
|
| Resin ID (ISO 1043) |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.31 | g/cm³ | ASTM D792 |
| Melt Volume-Flow Rate (MVR) (260°C/2.16 kg) | 8.50 to 11.7 | cm³/10min | ASTM D1238 |
| Molding Shrinkage - Flow (3.20 mm) | 1.5 to 1.7 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 2800 | MPa | ASTM D638 |
| Tensile Strength (Break, 23°C) | 54.0 | MPa | ASTM D638 |
| Tensile Elongation (Break, 23°C) | 150 | % | ASTM D638 |
| Flexural Modulus (23°C) | 2400 | MPa | ASTM D790 |
| Flexural Strength | 83.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 5.1 | kJ/m² | ASTM D256 |
| Notched Izod Impact (23°C) | 52 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 60.0 | °C | ASTM D648 |
| Melting Temperature 1 | 224 | °C | ASTM D2117 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 110 | °C | |
| Drying Time | 6.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Processing (Melt) Temp | 240 to 260 | °C | |
| Mold Temperature | 70.0 to 80.0 | °C |
| Note Message | |
|---|---|
| 1 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Marlex® 9005 | Chevron Phillips Chemical Company LLC | HDPE | Marlex® |
| Thanelene® TPU S80A15 PRTA010 TP305 MSP | Petropol Industry and Trade of Polymers LTDA | TPU-Polyester | Thanelene® TPU |
| VITAMIDE® AS30BK8522 | Jackdaw Polymers | Nylon 66 | VITAMIDE® |
| Lifolit® E 73.1340/2 glasklar | ELASTO | PVC, Flexible | Lifolit® |
| OP - PC/PBT 604-I | Oxford Polymers | PC+PBT | OP - PC/PBT |