Pibiflex® 2560 NATURALE
| Category: | TPC-ET , Thermoplastic Copolyester Elastomer |
| Manufacturer: | SO.F.TER. SPA |
| Trademark: | Pibiflex® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ZvA4e8_Pibiflex-2560-NATURALE.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Pibiflex® 2560 NATURALE is a Thermoplastic Copolyester Elastomer (TPC-ET) material. It is available in Europe, Latin America, or North America for injection molding. Primary attribute of Pibiflex® 2560 NATURALE: REACH Compliant. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.09 | g/cm³ | ASTM D792 |
| Melt Volume-Flow Rate (MVR) (220°C/2.16 kg) | 20.0 | cm³/10min | ASTM D1238 |
| Water Absorption (23°C, 24 hr) | 0.95 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D, 15 sec) | 27 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Break) | 16.0 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 800 | % | ASTM D638 |
| Flexural Modulus | 35.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ASTM D256 | ||
| -30°C | No Break | ||
| 23°C | No Break |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Peak Melting Temperature | 185 | °C | ASTM D3417 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | ASTM D257 | ||
| 23°C | 1.0E+13 | ohms·cm | |
| 100°C | 1.0E+11 | ohms·cm | |
| Dielectric Strength (2.00 mm) | 16 | kV/mm | ASTM D149 |
| Dielectric Constant | ASTM D150 | ||
| 1 kHz | 4.40 | ||
| 100 kHz | 4.30 | ||
| Dissipation Factor | ASTM D150 | ||
| 1 kHz | 5.0E-3 | ||
| 100 kHz | 0.014 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Oxygen Index | 20 | % | ASTM D2863 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 110 | °C | |
| Drying Time | 3.0 | hr | |
| Rear Temperature | 180 | °C | |
| Middle Temperature | 210 | °C | |
| Front Temperature | 220 | °C | |
| Mold Temperature | 40.0 to 60.0 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Ultramid® B3WG3 | BASF Corporation | Nylon 6 | Ultramid® |
| Nycal™ 1850L3H | Technical Polymers, LLC | Nylon 6 | Nycal™ |
| CompaDur® 121 GF 20 FR black (038) | DimeLika Plast GmbH | PBT | CompaDur® |
| CP PRYME® Polyethylene PE100HDC-20M | Chase Plastics Services Inc. | HDPE | CP PRYME® Polyethylene |
| Delta PC-1417 | Delta Polymers | PC | Delta |