CYCOLAC™ INP564 resin
| Category: | ABS+SAN , Acrylonitrile Butadiene Styrene + SAN |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | CYCOLAC™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ZswZQ7_CYCOLAC-INP564-resin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| SABIC INP564 provides compatibility with a wider range of ABS grades than many color concentrate bases; allows better dispersion than pellets; allows concentrate manufacturers to produce both pelletized and dry blend concentrate; provides a base resin with less heat history than pellets; suitable for direct weather exposure; can be used in all SAN applications where a fine particle size is desired. |
| General Information | |
|---|---|
| Features |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.08 | g/cm³ | ASTM D792 |
| -- | 1.07 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) | |||
| 230°C/3.8 kg | 38 | g/10 min | ASTM D1238 |
| 220°C/10.0 kg | 78 | g/10 min | ISO 1133 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 123 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 3890 | MPa | ASTM D638 |
| -- | 3840 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 2 | 52.0 | MPa | ASTM D638 |
| Yield | 54.1 | MPa | ISO 527-2/50 |
| Break 3 | 53.6 | MPa | ASTM D638 |
| Break | 54.1 | MPa | ISO 527-2/50 |
| Tensile Elongation | |||
| Yield 4 | 1.6 | % | ASTM D638 |
| Yield | 1.2 | % | ISO 527-2/50 |
| Break 5 | 1.7 | % | ASTM D638 |
| Break | 1.2 | % | ISO 527-2/50 |
| Flexural Modulus | |||
| 50.0 mm Span 6 | 3720 | MPa | ASTM D790 |
| -- 7 | 3460 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 65.4 | MPa | ISO 178 |
| Yield, 50.0 mm Span 8 | 82.5 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 1.1 | kJ/m² | ISO 179/2C |
| Notched Izod Impact | |||
| -30°C | 22 | J/m | ASTM D256 |
| 23°C | 14 | J/m | ASTM D256 |
| -30°C 9 | 2.5 | kJ/m² | ISO 180/1A |
| 23°C 10 | 1.9 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 95.2 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 3.20 mm | 83.4 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 11 | 85.3 | °C | ISO 75-2/Af |
| Vicat Softening Temperature | |||
| -- | 102 | °C | ISO 306/B50 |
| -- | 104 | °C | ISO 306/B120 |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | Type I, 5.0 mm/min |
| 3 . | Type I, 5.0 mm/min |
| 4 . | Type I, 5.0 mm/min |
| 5 . | Type I, 5.0 mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 2.0 mm/min |
| 8 . | 1.3 mm/min |
| 9 . | 80*10*4 |
| 10 . | 80*10*4 |
| 11 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SABIC® PPcompound 2500-6 | Saudi Basic Industries Corporation (SABIC) | PP, Unspecified | SABIC® PPcompound |
| Moplen EP300C | PolyMirae | PP, HMS | Moplen |
| EXPLORE® CT PP | Matrix Polymers | PP, Unspecified | EXPLORE® |
| Halar® 7114 | Solvay Specialty Polymers | ECTFE | Halar® |
| KOPLA PA66 KDP1000 | KOPLA Co., Ltd. | Nylon 66 | KOPLA PA66 |