Hytrel® 6646 NC010
| Category: | TPC-ET , THERMOPLASTIC POLYESTER ELASTOMER |
| Manufacturer: | DuPont Performance Polymers |
| Trademark: | Hytrel® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ZsZTgp_Hytrel-6646-NC010.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 66 Shore D High Performance Polyester Elastomer |
| General Information | |
|---|---|
| Additive |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Part Marking Code (ISO 11469) |
|
| Resin ID (ISO 1043) |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.23 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (240°C/2.16 kg) | 13 | g/10 min | ISO 1133 |
| Molding Shrinkage | ISO 294-4 | ||
| Across Flow | 1.4 | % | |
| Flow | 1.4 | % | |
| Water Absorption | ISO 62 | ||
| 23°C, 24 hr, 2.00 mm | 0.60 | % | |
| Equilibrium, 23°C, 2.00 mm, 50% RH | 0.20 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness | ISO 868 | ||
| Shore D | 66 | ||
| Shore D, 15 sec | 60 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 310 | MPa | ISO 527-2 |
| Tensile Stress | ISO 527-2 | ||
| Yield | 20.0 | MPa | |
| Break | 35.0 | MPa | |
| 10% Strain | 16.0 | MPa | |
| 100% Strain | 20.0 | MPa | |
| Tensile Strain | ISO 527-2 | ||
| Yield | 29 | % | |
| Break | > 300 | % | |
| Nominal Tensile Strain at Break | 380 | % | ISO 527-2 |
| Tensile Creep Modulus | ISO 899-1 | ||
| 1 hr | 260 | MPa | |
| 1000 hr | 190 | MPa |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C | 13 | kJ/m² | |
| 23°C, Partial Break | 110 | kJ/m² | |
| Charpy Unnotched Impact Strength (23°C) | No Break | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 87.0 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 45.0 | °C | ISO 75-2/A |
| Glass Transition Temperature 1 | 0.00 | °C | ISO 11357-2 |
| Vicat Softening Temperature | 100 | °C | ISO 306/B50 |
| Melting Temperature 2 | 211 | °C | ISO 11357-3 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flammability Classification | IEC 60695-11-10, -20 | ||
| 1.50 mm | HB | ||
| 3.00 mm | HB | ||
| Oxygen Index | 21 | % | ISO 4589-2 |
| Fill Analysis | Nominal Value | Unit | |
|---|---|---|---|
| Melt Density | 1.07 | g/cm³ | |
| Specific Heat Capacity of Melt | 2150 | J/kg/°C | |
| Thermal Conductivity of Melt | 0.15 | W/m/K |
| Additional Information | Nominal Value | Unit | |
|---|---|---|---|
| Effective Thermal Diffusivity | 0.0544 | cSt |
| Note Message | |
|---|---|
| 1 . | 10°C/min |
| 2 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 128 HI Z | RTP Company | PP, Unspecified | RTP |
| RheTech Polypropylene RCT120-01 | RheTech, Inc. | PP, Unspecified | RheTech Polypropylene |
| XYLEX™ X7300CL resin | SABIC Innovative Plastics Europe | PC+Polyester | XYLEX™ |
| Devcon DFense Blok™ Fast Cure (FC) | Devcon | Epoxy | Devcon |
| LNP™ LUBRICOMP™ KP003AXZ compound | SABIC Innovative Plastics | Acetal (POM) Homopolymer | LNP™ LUBRICOMP™ |