SABIC® LLDPE 518N
| Category: | LLDPE , Linear Low Density Polyethylene |
| Manufacturer: | Saudi Basic Industries Corporation (SABIC) |
| Trademark: | SABIC® LLDPE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Zs2fDr_SABIC-LLDPE-518N.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
SABIC® LLDPE 518N is a butene linear low density polyethylene resin. Films produced from this resin have high toughness, good puncture resistance, good heat sealing behaviour and excellent machinability on conversion lines. Application Typical applications for SABIC® LLDPE 518N are heavy duty shipping sacks, ice bags, frozen food bags, potato bags and agriculture films. This product is not intended for and must not be used in any pharmaceutical/medical applications. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.918 | g/cm³ | ISO 1183/A |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 0.50 | g/10 min | ISO 1133 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 50 | µm | |
| Tensile Modulus | ISO 527-3 | ||
| MD : 50 µm, blown film | 170 | MPa | ISO 527-3 |
| TD : 50 µm, blown film | 180 | MPa | ISO 527-3 |
| Tensile Stress | ISO 527-3 | ||
| MD : Yield, 50 µm, blown film | 11.0 | MPa | ISO 527-3 |
| TD : Yield, 50 µm, blown film | 11.0 | MPa | ISO 527-3 |
| MD : Broken, 50 µm, blown film | 40.0 | MPa | ISO 527-3 |
| TD : Broken, 50 µm, blown film | 32.0 | MPa | ISO 527-3 |
| Tensile Elongation | ISO 527-3 | ||
| MD : Broken, 50 µm, blown film | 550 | % | ISO 527-3 |
| TD : Broken, 50 µm, blown film | 800 | % | ISO 527-3 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Impact Strength - Blown Film (50.0 µm) | 270 | J/cm | ASTM D4272 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Puncture Resistance - Blown Film (50.0 µm) | 750 | J/m | Internal method |
| Tear Strength 1 | ISO 6383-2 | ||
| MD : 50.0 µm | 30.0 | kN/m | ISO 6383-2 |
| TD : 50.0 µm | 180.0 | kN/m | ISO 6383-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 104 | °C | ISO 306/A |
| Melting Temperature (DSC) | 120 | °C | Internal method |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°, 50.0 µm, Blown Film) | 55 | ASTM D2457 | |
| Haze (50.0 µm, Blown Film) | 13 | % | ASTM D1003A |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film of 50 µm and BUR=2 has been produced on Kiefel IBC with 130 kg/h. Die size 200 mm, die gap 2,7 mm. |
| Note Message | |
|---|---|
| 1 . | Blown Film |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TEKAMID™ TB120G60W | Mando Advanced Materials Co., Ltd. | Nylon 6 | TEKAMID™ |
| Cheng Yu PP237G2 | Cheng Yu Plastic Company Limited | PP, Unspecified | Cheng Yu |
| HiFill® PA12 GF30 HS L | Techmer Engineered Solutions | Nylon 12 | HiFill® |
| Lustran® ABS 256 | INEOS ABS (USA) | ABS | Lustran® ABS |
| Alathon® M6010-2 | LyondellBasell Industries | HDPE, MMW | Alathon® |