UmaPET AO/AI Datasheet,PET,Ester Industries Ltd.-SHANGHAI SUSHENG

Message
Key Features UmaPET AO/AI is transparent film with one-side Chemical coated. The film possesses good thermal, mechanical, optical and surface properties along with excellent transparency and dimensional stability. Application This film is widely used for high quality, Printing and Lamination applications. The film shows enhanced adhesion to wide range of inks, adhesives and other primer/coatings. This film meets customer's stringent requirements of high ink adhesion and superior bond strength in laminates.

General Information
Features	Bondability Excellent Printability Good Adhesion Good Dimensional Stability Good Surface Finish High Clarity Opticals
Uses	Coating Applications Film Laminates
Appearance	Clear/Transparent
Forms	Film

Physical	Nominal Value	Unit	Test Method
Molding Shrinkage			ASTM D1204
Flow : 150°C, 30 min, 0.0100 mm	2.5	%
Flow : 150°C, 30 min, 0.0120 mm	2.5	%
Flow : 150°C, 30 min, 0.0150 mm	2.5	%
Flow : 150°C, 30 min, 0.0230 mm	2.5	%
Across Flow : 150°C, 30 min, 0.0100 mm	0.40	%
Across Flow : 150°C, 30 min, 0.0120 mm	0.40	%
Across Flow : 150°C, 30 min, 0.0150 mm	0.40	%
Across Flow : 150°C, 30 min, 0.0230 mm	0.40	%

Mechanical	Nominal Value	Test Method
Coefficient of Friction		ASTM D1894
vs. Itself - Dynamic ¹	0.40
vs. Itself - Dynamic ²	0.40
vs. Itself - Dynamic ³	0.40
vs. Itself - Dynamic ⁴	0.38
vs. Itself - Static ⁵	0.48
vs. Itself - Static ⁶	0.48
vs. Itself - Static ⁷	0.48
vs. Itself - Static ⁸	0.46

Films	Nominal Value	Unit	Test Method
Film Thickness - Tested	10 12 15 23	µm
Film Thickness - Recommended / Available	10, 12, 15, 23 µm
Tensile Strength			ASTM D882
MD : Break, 10 µm	206	MPa
MD : Break, 12 µm	206	MPa
MD : Break, 15 µm	186	MPa
MD : Break, 23 µm	186	MPa
TD : Break, 10 µm	216	MPa
TD : Break, 12 µm	216	MPa
TD : Break, 15 µm	206	MPa
TD : Break, 23 µm	206	MPa
Tensile Elongation			ASTM D882
MD : Break, 10 µm	100	%
MD : Break, 12 µm	100	%
MD : Break, 15 µm	100	%
MD : Break, 23 µm	100	%
TD : Break, 10 µm	90	%
TD : Break, 12 µm	90	%
TD : Break, 15 µm	90	%
TD : Break, 23 µm	90	%
Yield			Internal Method
10.0 µm	71.4	m²/kg
12.0 µm	59.5	m²/kg
15.0 µm	47.6	m²/kg
23.0 µm	31.0	m²/kg

Additional Information	Nominal Value	Unit	Test Method
Wetting Tension			ASTM D2578
Coated side : 10.0 µm	40	dyne/cm
Coated side : 12.0 µm	40	dyne/cm
Coated side : 15.0 µm	40	dyne/cm
Coated side : 23.0 µm	40	dyne/cm
Plain side : 10.0 µm	44	dyne/cm
Plain side : 12.0 µm	44	dyne/cm
Plain side : 15.0 µm	44	dyne/cm
Plain side : 23.0 µm	44	dyne/cm

Optical	Nominal Value	Unit	Test Method
Haze			ASTM D1003
10.0 µm	3.5	%
12.0 µm	3.5	%
15.0 µm	3.5	%
23.0 µm	4.5	%

Category:	PET , Polyethylene Terephthalate
Manufacturer:	Ester Industries Ltd.
Trademark:	UmaPET
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	Zqvolo_UmaPET-AO-AI.pdf
PRICE:	Order Products email sales@su-jiao.com

Resin Grade	Manufacturer	Category	Trademark
SABIC® LLDPE MG500026	Saudi Basic Industries Corporation (SABIC)	LLDPE	SABIC® LLDPE
Nanjing Hongrui PC CS500	Nanjing Hongrui Engineering Plastics Co., Ltd.	PC Alloy	Nanjing Hongrui PC
KPOL-LDPE LD K-0.30/921	KPOL Chem Co.	LDPE	KPOL-LDPE
Lionpol HF-207565	Lion Polymers Incorporated	TPE	Lionpol
EPALINE 393A34	Epaflex Polyurethanes S.R.L.	TPU-Polyester	EPALINE