Ablefilm ECF550X
| Category: | Epoxy , Epoxy; Epoxide |
| Manufacturer: | Henkel Ablestik |
| Trademark: | Ablefilm |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ZpD8qL_Ablefilm-ECF550X.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
ABLEFILM® ECF550X silver filled, epoxy adhesive film is designed for microelectronic applications which require electrical conductivity. This material exhibits conductivity in the x, y, and z axes. When used for substrate attach, ECF550X acts as an electrical ground plane. It provides RF/EMI shielding. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Physical | Nominal Value | Test Method | |
|---|---|---|---|
| pH | 4.5 | Internal Method |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Electrical Resistivity 1 | 0.00200 | ohms/in² |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Carrier | Glass Fabric | ||
| Ionic Chloride (100°C) 2 | 35 | ppm | Internal Method |
| Ionic Potassium (100°C) 3 | 5 | ppm | |
| Ionic Sodium (100°C) 4 | 15 | ppm | Internal Method |
| Lap Shear | Internal Method | ||
| Al to Al : 25°C | 15.2 | MPa | |
| Au to Au : 25°C | 14.5 | MPa | |
| Water Extract Conductivity 5 | 25.0 | µS/cm | Internal Method |
| Weight Loss on Heating (300°C) 6 | 0.20 | % | Internal Method |
| Work Life (25°C) 7 | 3.0 | day | Internal Method |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Glass Transition Temperature | 109 | °C | Internal Method |
| CLTE - Flow | Internal Method | ||
| < 109°C | 4.0E-5 | cm/cm/°C | |
| > 109°C | 5.0E-5 | cm/cm/°C | |
| Thermal Conductivity 8(121°C) | 2.1 | W/m/K | Internal Method |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity 9 | 8.0E-3 | ohms·cm | Internal Method |
| Thermoset | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Pot Life (23°C) | 4300 | min | |
| Shelf Life (-40°C) | 52 | wk | |
| Demold Time | |||
| 125°C | 120 | min | |
| 150°C | 60 | min | |
| Post Cure Time | |||
| 52°C | 2.0 | hr | |
| 66°C | 1.0 | hr |
| Note Message | |
|---|---|
| 1 . | Measured through Gold Joints |
| 2 . | Teflon fl ask, 5 gm sample/20-40 mesh, 50 gm DI water, 24 hours |
| 3 . | Teflon fl ask, 5 gm sample/20-40 mesh, 50 gm DI water, 24 hours |
| 4 . | Teflon fl ask, 5 gm sample/20-40 mesh, 50 gm DI water, 24 hours |
| 5 . | Conductometer |
| 6 . | Thermogravimetric Analysis |
| 7 . | 25% increase in viscosity @ RT |
| 8 . | C-MATIC conductance tester |
| 9 . | 4-point probe |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Propafilm™ MTX90 | Innovia Films Ltd. | PP Alloy | Propafilm™ |
| VITAMIDE® BG32WT6565 | Jackdaw Polymers | Nylon 6 | VITAMIDE® |
| Celstran® PPS-CF40-01 | Celanese Corporation | PPS | Celstran® |
| Karina IVORY PVC COMPOUND -E 670D35/ 1-A-AT-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| ALTECH® PP-H A 2030/169 GF30 CP | ALBIS PLASTIC GmbH | PP Homopolymer | ALTECH® PP-H |