SCHULABLEND® (ASA/PA) M/MW NC 100 SF K2083
| Category: | ASA+Nylon , Acrylonitrile Styrene Acrylate + Nylon |
| Manufacturer: | A. Schulman Europe |
| Trademark: | SCHULABLEND® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Zp1POv_SCHULABLEND-ASA-PA-M-MW-NC-100-SF-K2083.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Nanocomposite based on ASA/PA 6-blend with increased dimensional stability, high flow, UV stabilized |
| General Information | |
|---|---|
| Processing Method |
|
| Resin ID (ISO 1043) |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.17 | g/cm³ | ISO 1183/A |
| Melt Volume-Flow Rate (MVR) (250°C/5.0 kg) | 20.3 | cm³/10min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 3240 | MPa | ISO 527-2/1A/1 |
| Tensile Stress | ISO 527-2/1A/50 | ||
| Yield | 50.5 | MPa | ISO 527-2/1A/50 |
| Fracture | 48.0 | MPa | ISO 527-2/1A/50 |
| Tensile Strain (Yield) | 2.8 | % | ISO 527-2/1A/50 |
| Nominal Tensile Strain at Break | 25 | % | ISO 527-2/1A/50 |
| Flexural Modulus 1 | 3000 | MPa | ISO 178 |
| Flexural Stress 2 | 75.6 | MPa | ISO 178 |
| Flexural Strain at Flexural Strength | 5.1 | % | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 10 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 38 | kJ/m² | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 106 | °C | ISO 75-2/Bf |
| 1.8 MPa, not annealed | 70.0 | °C | ISO 75-2/Af |
| Vicat Softening Temperature | 120 | °C | ISO 306/B50 |
| Additional Information |
|---|
| 1.) Not for use in food contact applications2.) Not for use in medical or pharmaceutical applications |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TOTAL Polypropylene PPR Z9450 | TOTAL Refining & Chemicals | PP Random Copolymer | TOTAL Polypropylene |
| Multi-Flex® TEA A 6003 ACN1 | Multibase, A Dow Corning Company | TPE | Multi-Flex® TEA |
| Axiall PVC 8150 White 91 | Axiall Corporation | PVC, Rigid | Axiall PVC |
| Lupolen 1800 H | LyondellBasell Industries | LDPE | Lupolen |
| Mafill® CT 4210 | Ravago Group | PP Copolymer | Mafill® |