Prime PE HMWPE 1000 Swirl

Category:	HMWPE , High Molecular Weight Polyethylene
Manufacturer:	Primex Plastics Corporation
Trademark:	Prime PE
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	ZoGZie_Prime-PE-HMWPE-1000-Swirl.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

Message
This product consists of a HMWPE substrate with a three-color swirlcap of HMWPE. The swirl can beon one or both sides of the sheet.The thickness can be varied to suityour specific material requirementsand draw ratios. Applications: Applications so far have consisted of playground equipment, camouflage deer blinds, canoes, and other sporting equipment. Processing: This is a crystalline material, therefore, good forming practices should be applied when forming this product. Forming temperature is 310-360°F. Mold temperature should be 160-200°F. Aluminum mold with grit blasted surface is preferred. The tool should be designed with a moat on the outsideof the trim line. Mold shrink is .016 -.028 in/in. Finishing: Prime HMWPE 1000 Swirl can be fabricated by using techniques such as; drilling, routing, punching, sawing and cutting with a die, laser or water jet. Mechanical screws and other type of fasteners can be used. The CLTE is high, therefore, movement of the part must be considered. Please contact your Primex Plastics representative formore information on finishing,fabricating, or the thermoforming process. Colors, Textures and Capabilities: Prime HMWPE 1000 Swirl can be color matched to meet your specific requirements. Prime HMWPE 1000 Swirl is extruded in gauges of .100 to .300 and up to 90" in width.Textures include; Smooth or Levant ll.

Message

This product consists of a HMWPE substrate with a three-color swirlcap of HMWPE. The swirl can beon one or both sides of the sheet.The thickness can be varied to suityour specific material requirementsand draw ratios.

Applications:
Applications so far have consisted of playground equipment, camouflage deer blinds, canoes, and other sporting equipment.

Processing:
This is a crystalline material, therefore, good forming practices should be applied when forming this product. Forming temperature is 310-360°F. Mold temperature should be 160-200°F. Aluminum mold with grit blasted surface is preferred. The tool should be designed with a moat on the outsideof the trim line. Mold shrink is .016 -.028 in/in.

Finishing:
Prime HMWPE 1000 Swirl can be fabricated by using techniques such as; drilling, routing, punching, sawing and cutting with a die, laser or water jet. Mechanical screws and other type of fasteners can be used. The CLTE is high, therefore, movement of the part must be considered.

Please contact your Primex Plastics representative formore information on finishing,fabricating, or the thermoforming process.

Colors, Textures and Capabilities:
Prime HMWPE 1000 Swirl can be color matched to meet your specific requirements. Prime HMWPE 1000 Swirl is extruded in gauges of .100 to .300 and up to 90" in width.Textures include; Smooth or Levant ll.

General Information
Features	Crystalline High Molecular Weight
Uses	Sporting Goods
Agency Ratings	FDA 21 CFR 177.1520
Appearance	Colors Available
Forms	Sheet

Physical	Nominal Value	Unit	Test Method
Specific Gravity	0.947	g/cm³	ASTM D792
Molding Shrinkage - Flow	1.6 to 2.8	%
Environmental Stress-Cracking Resistance (F50)	> 600	hr	ASTM D1693A

Mechanical	Nominal Value	Unit	Test Method
Tensile Strength (Yield)	24.8	MPa	ASTM D638
Tensile Elongation (Break)	> 600	%	ASTM D638
Flexural Modulus	1170	MPa	ASTM D790

Thermal	Nominal Value	Unit	Test Method
Brittleness Temperature	< -90.6	°C	ASTM D746
Vicat Softening Temperature	124	°C	ASTM D1525

Flammability	Nominal Value		Test Method
Flame Rating ¹(1.52 mm)	HB		UL 94
Flammability (> 1.52 mm)	Pass		FMVSS 302

Additional Information	Nominal Value	Unit
Forming Temperature	154 to 182	°C
Mold Temperature (other)	71 to 93	°C

Note Message
1 .	>0.060 in

Resin Grade	Manufacturer	Category	Trademark
Polytech & Net XP 9200	Polytech & Net Gmbh	mLLDPE	Polytech & Net
WELLAMID Nylon 6000 HWV0CP	CP-Polymer-Technik GmbH & Co. KG	Nylon 6	WELLAMID Nylon
Huafon JF-D-8603	Huafon Group Co., Ltd.	PUR, Unspecified	Huafon
KOPA® KN3311BLK	Kolon Plastics, Inc.	Nylon 66	KOPA®
Jampilen RC1601	Jam Polypropylene Company	PP Random Copolymer	Jampilen