Category:	LDPE , Low Density Polyethylene
Manufacturer:	Borealis AG
Trademark:	Borealis
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	ZnsDG0_Borealis-LE6025.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

WECHAT

Message

Black low density polyethylene jacketing compound for energy and communication cables

LE6025 is a black low density copolymer modified polyethylene compound. It is characterized by excellent stress crack resistance and mechanical properties and low temperature performance in combination with good extrudability.

LE6025 contains 2,5% well dispersed furnace black of nominal particle size less than 25 nanometres in order to ensure excellent weathering resistance.

Applications

Jacket for energy and communication cables

Specifications
LE6025 meets the applicable requirements as below when processed using sound extrusion practice and testing procedure:

ISO 1872-PE, KCHL, 18-D003

ASTM D 1248 Type I, Class C, Category 5, Grade E5, J3, W2-4

The following cable material standards are met by LE6025:

EN 50290-2-24

Cables manufactured with LE6025 using sound extrusion practice normally comply with the following cable product standards:

IEC 60502, Part 2, Type ST3

IEC 60840, Type ST3

HD 603 S1, DMP 7, 8

HD 620 S2, Part 1, table 4B, DMP 10, 12, 14, 17

General Information
Features	Copolymer Good Flexibility Good Surface Finish Good Weather Resistance High ESCR (Stress Crack Resist.) Low Density
Uses	Cable Jacketing
Agency Ratings	ASTM D 1248, I, Class C, Cat. 5 Grade E5, J3, W2-4 HD 620 S1 DMP 7, 8 IEC 60502-2 Type ST3 IEC 60840 Type ST3 ISO 1872 PE KCHL 18D003
Appearance	Black
Forms	Granules
Processing Method	Extrusion

Physical	Nominal Value	Unit	Test Method
Density			ISO 1183
-- ¹	0.933	g/cm³
Base Resin	0.921	g/cm³
Melt Mass-Flow Rate (MFR) (190°C/2.16 kg)	0.35	g/10 min	ISO 1133
Environmental Stress-Cracking Resistance (50°C, 10% Igepal, F20)	> 2500	hr	IEC 60811-4-1/B

Hardness	Nominal Value	Unit	Test Method
Shore Hardness (Shore D, 1 sec)	50		ISO 868

Mechanical	Nominal Value	Unit	Test Method
Tensile Stress (Yield)	> 25.0	MPa	ISO 527-2/50
Tensile Strain (Break)	> 900	%	ISO 527-2/50
Flexural Modulus	300	MPa	ASTM D790

Thermal	Nominal Value	Unit	Test Method
Brittleness Temperature	< -76.0	°C	ASTM D746

Electrical	Nominal Value	Unit	Test Method
Volume Resistivity	1.0E+16	ohms·cm	IEC 60093
Electric Strength	20	kV/mm	IEC 60243-1

Note Message
1 .	Compound

Resin Grade	Manufacturer	Category	Trademark
Sinvicomp SIG3572	Teknor Apex Asia Pacific PTE. LTD.	PVC, Flexible	Sinvicomp
Weifang Kingdom CPET101	Weifang Kingdom Plastic Co., Ltd	CPE	Weifang Kingdom
TOTAL Polyethylene LDPE LA 0710	TOTAL Refining & Chemicals	LDPE	TOTAL Polyethylene
ASTALAC™ ABS MDA49	Marplex Australia Pty. Ltd.	ABS	ASTALAC™
Sarlink® TPE ME-2655B (PRELIMINARY DATA)	Teknor Apex Company	TPE	Sarlink® TPE