LNP™ COLORCOMP™ 310C compound
| Category: | PBT , Polybutylene Terephthalate |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ COLORCOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ZlGkQD_LNPCOLORCOMP310Ccompound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP* COLORCOMP* 310C is an unreinforced compound based on PBT resin. Added feature of this grade is a typical viscosity of 5000-7000. |
| General Information | |
|---|---|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.31 | g/cm³ | ASTM D792 |
| Specific Volume | 0.770 | cm³/g | ASTM D792 |
| Molding Shrinkage | Internal method | ||
| Flow 1 | 0.90 - 1.6 | % | Internal method |
| Flow 2 | 1.5 - 2.3 | % | Internal method |
| Transverse flow 3 | 1.0 - 1.7 | % | Internal method |
| Transverse flow 4 | 1.6 - 2.4 | % | Internal method |
| Water Absorption (24 hr) | 0.080 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 117 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 5 | ASTM D638 | ||
| Yield | 51.7 | MPa | ASTM D638 |
| Fracture | 51.7 | MPa | ASTM D638 |
| Tensile Elongation 6(Break) | 300 | % | ASTM D638 |
| Flexural Modulus 7(50.0 mm Span) | 2340 | MPa | ASTM D790 |
| Flexural Strength 8 | ASTM D790 | ||
| Yield, 50.0mm span | 82.7 | MPa | ASTM D790 |
| Fracture, 50.0mm span | 82.7 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 53 | J/m | ASTM D256 |
| Unnotched Izod Impact (23°C) | 1600 | J/m | ASTM D4812 |
| Dart Drop Impact | ASTM D3029 | ||
| 23°C | 40.7 | J | ASTM D3029 |
| 23°C 9 | 40.7 | J | ASTM D3029 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, unannealed, 6.40mm | 154 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 6.40mm | 54.4 | °C | ASTM D648 |
| CLTE - Flow | ASTM E831 | ||
| -40 to 40°C | 8.1E-5 | cm/cm/°C | ASTM E831 |
| 60 to 138°C | 1.4E-4 | cm/cm/°C | ASTM E831 |
| RTI Elec | 120 | °C | UL 746 |
| RTI Imp | 120 | °C | UL 746 |
| RTI | 140 | °C | UL 746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | > 4.0E+16 | ohms·cm | ASTM D257 |
| Dielectric Strength | ASTM D149 | ||
| 1.60 mm, in Air | 23 | kV/mm | ASTM D149 |
| 1.60 mm, in Oil | 23 | kV/mm | ASTM D149 |
| 3.20 mm, in Air | 16 | kV/mm | ASTM D149 |
| 3.20 mm, in Oil | 16 | kV/mm | ASTM D149 |
| Dielectric Constant | ASTM D150 | ||
| 100 Hz | 3.30 | ASTM D150 | |
| 1 MHz | 3.10 | ASTM D150 | |
| Dissipation Factor | ASTM D150 | ||
| 100 Hz | 2.0E-3 | ASTM D150 | |
| 1 MHz | 0.020 | ASTM D150 | |
| Arc Resistance 10 | PLC 5 | ASTM D495 | |
| Comparative Tracking Index (CTI) | PLC 0 | UL 746 | |
| High Voltage Arc Tracking Rate (HVTR) | PLC 1 | UL 746 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.5 mm) | HB | UL 94 |
| Fill Analysis | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melt Viscosity | 600 | Pa·s | Internal method |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 3.0 - 4.0 | hr | |
| Drying Time, Maximum | 12 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Suggested Shot Size | 40 - 80 | % | |
| Rear Temperature | 232 - 249 | °C | |
| Middle Temperature | 238 - 254 | °C | |
| Front Temperature | 243 - 260 | °C | |
| Nozzle Temperature | 238 - 254 | °C | |
| Processing (Melt) Temp | 243 - 260 | °C | |
| Mold Temperature | 49 - 77 | °C | |
| Back Pressure | 0.345 - 0.689 | MPa | |
| Screw Speed | 50 - 100 | rpm | |
| Vent Depth | 0.013 - 0.025 | mm |
| Note Message | |
|---|---|
| 1 . | 0.75 to 2.3 mm |
| 2 . | 2.3 to 4.6 mm |
| 3 . | 0.75 to 2.3 mm |
| 4 . | 2.3 to 4.6 mm |
| 5 . | Type 1, 50mm/min |
| 6 . | Type 1, 50mm/min |
| 7 . | 1.3 mm/min |
| 8 . | 1.3 mm/min |
| 9 . | Modified |
| 10 . | Tungsten electrode |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| ANSAGLAS A07 000 0000 000 A | Daloga srl | Acrylic (PMMA) | ANSAGLAS |
| CERTENE™ HGB-0454 | Muehlstein | HDPE | CERTENE™ |
| ExxonMobil™ HDPE HD 9856B | ExxonMobil Chemical | HDPE, UHMW | ExxonMobil™ HDPE |
| REV Materials 8001-003 | REV Materials | PP, Unspecified | REV Materials |
| POCAN® A 3131 000000 | LANXESS Corporation | PBT+ASA | POCAN® |