Ferro PP RPP30GT13UL NATURAL
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | Ferro Corporation |
| Trademark: | Ferro PP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ZkfUlA_Ferro-PP-RPP30GT13UL-NATURAL.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Ferro PP RPP30GT13UL NATURAL is a polypropylene material,. This product is available in North America, Africa and the Middle East, Latin America, Europe or Asia Pacific. The processing method is injection molding. The main features of Ferro PP RPP30GT13UL NATURAL are:
|
| General Information | |
|---|---|
| Features |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.45 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 8.5 | g/10 min | ASTM D1238 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (23°C) | 44.8 | MPa | ASTM D638 |
| Tensile Elongation (Break, 23°C) | 4.0 | % | ASTM D638 |
| Flexural Modulus | ASTM D790 | ||
| 1% secant : 23°C | 5180 | MPa | ASTM D790 |
| Tangent : 23°C | 5240 | MPa | ASTM D790 |
| Flexural Strength (23°C) | 68.9 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 130 | J/m | ASTM D256 |
| Unnotched Izod Impact (23°C) | 430 | J/m | ASTM D4812 |
| Dart Drop Impact (23°C) | 0.791 | J | ASTM D5420 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, not annealed | 149 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 132 | °C | ASTM D648 |
| RTI Elec (1.59 mm) | 110 | °C | UL 746 |
| RTI Imp (1.59 mm) | 110 | °C | UL 746 |
| RTI (1.59 mm) | 110 | °C | UL 746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Arc Resistance | 137 | sec | ASTM D495 |
| Comparative Tracking Index (CTI) | 600 | V | UL 746 |
| High Voltage Arc Tracking Rate (HVTR) | 0.00 | mm/min | UL 746 |
| Hot-wire Ignition (HWI) | 100 | sec | UL 746 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.59 mm) | V-0 | UL 94 |
| Additional Information |
|---|
| The value listed as Comparative Tracking Index was tested in accordance with ASTM D3638. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 1605 TFE 15 | RTP Company | PAS | RTP |
| Vinnolit® E 2078 | Vinnolit GmbH & Co. KG | PVC, Unspecified | Vinnolit® |
| Next Nylon 66 Prime Series PMTHS-01BK | Next Polymers Ltd. | Nylon 66 | Next Nylon 66 Prime Series |
| Geon™ Vinyl Flexible XV3645 | PolyOne Corporation | PVC, Flexible | Geon™ Vinyl Flexible |
| INFUSE™ 9807 | The Dow Chemical Company | OBC | INFUSE™ |