| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Lucent Polymers, Inc. |
| Trademark: | Lucent PA |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ZkTlZD_Lucent-PA-G6-15.pdf |
| PRICE: | Order Products email sales@su-jiao.com |
| Message |
|---|
|
15% Glass Fiber Reinforced, Nylon 6 Colors Available Add "H" for Heat Stabilized Add "HU" for Weatherable Typical Properties, Dry as Molded |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Appearance |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.23 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.18 mm) | 0.80 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield) | 96.5 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 4.0 | % | ASTM D638 |
| Flexural Modulus | 4140 | MPa | ASTM D790 |
| Flexural Strength | 145 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.18 mm) | 59 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 188 | °C | ASTM D648 |
| Peak Melting Temperature | 216 to 225 | °C | ASTM D789 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sinvicomp SRF9711 | Teknor Apex Asia Pacific PTE. LTD. | PVC, Rigid | Sinvicomp |
| Vinnolit® E 70 CQ | Vinnolit GmbH & Co. KG | PVC Homopolymer | Vinnolit® |
| DOMAMID® 6ST1HUV | DOMO Engineering Plastics SPA | Nylon 6 | DOMAMID® |
| KRATON® D4433 P | Kraton Polymers LLC | SIS | KRATON® |
| Sylvin 8350-73 Natural | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |