Apec® 1603
| Category: | PC , Polycarbonate |
| Manufacturer: | Covestro - Polycarbonates |
| Trademark: | Apec® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Zi8Fqe_Apec-1603.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| MVR (330°C/2.16kg) 25 cm³/10 min; high viscosity; UV stabilized; softening temperature (VST/B 120)=159 °C; injection molding - melt temperature 320 - 340°C |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 1.18 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (330°C/2.16 kg) | 26 | g/10 min | ISO 1133 |
| Melt Volume-Flow Rate (MVR) (330°C/2.16 kg) | 25.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage 1 | ISO 294-4 | ||
| Across Flow : 2.00 mm | 0.75 | % | |
| Flow : 2.00 mm | 0.75 | % | |
| Water Absorption | ISO 62 | ||
| Saturation, 23°C | 0.40 | % | |
| Equilibrium, 23°C, 50% RH | 0.20 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Ball Indentation Hardness | 115 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 2300 | MPa | ISO 527-2/1 |
| Tensile Stress (Yield, 23°C) | 65.0 | MPa | ISO 527-2/50 |
| Tensile Strain (Yield, 23°C) | 7.0 | % | ISO 527-2/50 |
| Nominal Tensile Strain at Break (23°C) | > 50 | % | ISO 527-2/50 |
| Flexural Modulus 2(23°C) | 2200 | MPa | ISO 178 |
| Flexural Stress 3(23°C) | 95.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -30°C | No Break | ||
| 23°C | No Break |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 151 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 139 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 159 | °C | ISO 306/B120 |
| CLTE | ISO 11359-2 | ||
| Flow : 23 to 55°C | 7.0E-5 | cm/cm/°C | |
| Transverse : 23 to 55°C | 7.0E-5 | cm/cm/°C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+16 | ohms | IEC 60093 |
| Volume Resistivity (23°C) | 1.0E+16 | ohms·cm | IEC 60093 |
| Electric Strength (23°C, 1.00 mm) | 35 | kV/mm | IEC 60243-1 |
| Relative Permittivity | IEC 60250 | ||
| 23°C, 100 Hz | 3.00 | ||
| 23°C, 1 MHz | 3.00 | ||
| Dissipation Factor | IEC 60250 | ||
| 23°C, 100 Hz | 1.6E-3 | ||
| 23°C, 1 MHz | 8.7E-3 | ||
| Comparative Tracking Index | IEC 60112 | ||
| Solution A | 250 | V | |
| Solution B | < 100 | V |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.50 mm | HB | ||
| 3.00 mm | HB | ||
| Glow Wire Flammability Index | 850 | °C | IEC 60695-2-12 |
| Oxygen Index 4 | 24 | % | ISO 4589-2 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Refractive Index 5 | 1.581 | ISO 489 | |
| Transmittance (1000 µm) | 90.0 | % | ISO 13468-2 |
| Additional Information | Nominal Value | Test Method | |
|---|---|---|---|
| Electrolytical Corrosion (23°C) | A1 | IEC 60426 |
| Note Message | |
|---|---|
| 1 . | 60x60x2 mm |
| 2 . | 2.0 mm/min |
| 3 . | 2.0 mm/min |
| 4 . | Procedure A |
| 5 . | Method A |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sicoklar E71.22 | Ravago Group | PC | Sicoklar |
| Sinvicomp SRP5602 | Teknor Apex Asia Pacific PTE. LTD. | PVC, Rigid | Sinvicomp |
| Sylvin 8200-65 Black | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Delta N66 UT | Delta Polymers | Nylon 66 | Delta |
| Geon™ Vinyl Flexible F78E | PolyOne Corporation | PVC, Flexible | Geon™ Vinyl Flexible |