Plexar® PX2220

Category:	HDPE , High Density Polyethylene
Manufacturer:	LyondellBasell Industries
Trademark:	Plexar®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	ZhdG41_Plexar-PX2220.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

Message
Plexar tie-layers are chemically modified resins used to bond unlike materials, primarily in packaging and industrial applications. Common adherents include polyethylene resins and copolymers, EVA, EMA, polypropylene, polyamide (nylon), ethylene vinyl alcohol copolymers (EVOH), ionomer and other sealants, polyethylene terephthalate (PET) resins and copolymers, styrenic polymers, metal, and paperboard. Product grades primarily used for blown and cast films, sheet and thermoforming, blow molding, extrusion coating and lamination, tubing, pipe, and other specialty applications are available in pellet form. Contact your Plexar sales and/or Equistar technical service representative for more information and specific recommendations for your application(s).

Message

Plexar tie-layers are chemically modified resins used to bond unlike materials, primarily in packaging and industrial applications. Common adherents include polyethylene resins and copolymers, EVA, EMA, polypropylene, polyamide (nylon), ethylene vinyl alcohol copolymers (EVOH), ionomer and other sealants, polyethylene terephthalate (PET) resins and copolymers, styrenic polymers, metal, and paperboard. Product grades primarily used for blown and cast films, sheet and thermoforming, blow molding, extrusion coating and lamination, tubing, pipe, and other specialty applications are available in pellet form. Contact your Plexar sales and/or Equistar technical service representative for more information and specific recommendations for your application(s).

General Information
Uses	Adhesives Food Packaging Industrial Applications Packaging
Agency Ratings	FDA 21 CFR 175.105
Forms	Pellets
Processing Method	Extrusion

Physical	Nominal Value	Unit	Test Method
Density	0.943	g/cm³	ASTM D1505
Melt Mass-Flow Rate (MFR) (190°C/2.16 kg)	6.0	g/10 min	ASTM D1238

Mechanical	Nominal Value	Unit	Test Method
Tensile Strength (Break)	17.2	MPa	ASTM D638
Tensile Elongation (Break)	25	%	ASTM D638
Flexural Modulus - 1% Secant	545	MPa	ASTM D790

Thermal	Nominal Value	Unit	Test Method
Vicat Softening Temperature	112	°C	ASTM D1525
Oxidation Induction Time	> 20	min	ASTM D3985

Extrusion	Nominal Value	Unit
Melt Temperature	> 210	°C

Resin Grade	Manufacturer	Category	Trademark
RTP 1200-65D TFE 10	RTP Company	TPU-Polyester	RTP
Radilon® S RV300K 333 NER	Radici Plastics	Nylon 6	Radilon®
Tecomid® NA40 NL IM	Eurotec Engineering Plastics	Nylon 66	Tecomid®
LEXAN™ EXL1434 resin	SABIC Innovative Plastics	PC	LEXAN™
SD POLYCA™ LD2050-AAH12	Sumika Styron Polycarbonate Limited	PC	SD POLYCA™