| Super Toughened, Heat Stabilized, Polyamide 66 |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Part Marking Code (ISO 11469) |
|
| Resin ID (ISO 1043) |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.08 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | |||
| Across Flow | 1.8 | -- | % | |
| Across Flow : 80°C, 48 hr | 0.050 | -- | % | |
| Flow | 2.0 | -- | % | |
| Flow : 80°C, 48 hr | 0.050 | -- | % | |
| Water Absorption | ||||
| 24 hr | 1.1 | -- | % | ASTM D570 |
| 23°C, 24 hr, 2.00 mm | 6.7 | -- | % | ISO 62 |
| Equilibrium, 23°C, 2.00 mm, 50% RH | 2.0 | -- | % | ISO 62 |
| Hardness | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Ball Indentation Hardness (H 358/30) | 104 | -- | MPa | ISO 2039-1 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 2000 | 900 | MPa | ISO 527-2 |
| Tensile Stress | ISO 527-2 | |||
| Yield | 52.0 | -- | MPa | |
| 50% Strain | -- | 45.0 | MPa | |
| Tensile Strain | ISO 527-2 | |||
| Yield | 4.0 | -- | % | |
| Break | -- | > 50 | % | |
| Nominal Tensile Strain at Break | 50 | -- | % | ISO 527-2 |
| Flexural Modulus | 1900 | 800 | MPa | ISO 178 |
| Films | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Elongation - MD (Yield) | 4.4 | -- | % | ISO 527-3 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -30°C | 20 | 17 | kJ/m² | |
| 23°C | 80 | 110 | kJ/m² | |
| Charpy Unnotched Impact Strength (23°C) | No Break | No Break | ISO 179/1eU | |
| Notched Izod Impact Strength | ISO 180/1A | |||
| -40°C | 19 | 16 | kJ/m² | |
| 23°C | 75 | 95 | kJ/m² | |
| Tensile Impact Strength (23°C) | 600 | -- | kJ/m² | ISO 8256/1 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, Unannealed | 157 | -- | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 62.0 | -- | °C | ISO 75-2/A |
| Glass Transition Temperature 1 | 75.0 | -- | °C | ISO 11357-2 |
| Melting Temperature 2 | 262 | -- | °C | ISO 11357-3 |
| CLTE | ISO 11359-2 | |||
| Flow | 9.0E-5 | -- | cm/cm/°C | |
| Transverse | 1.2E-4 | -- | cm/cm/°C |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | -- | 5.0E+12 | ohms | IEC 60093 |
| Volume Resistivity | > 1.0E+15 | 2.7E+12 | ohms·cm | IEC 60093 |
| Electric Strength | 24 | 24 | kV/mm | IEC 60243-1 |
| Relative Permittivity | IEC 60250 | |||
| 100 Hz | 3.50 | 6.20 | ||
| 1 MHz | 3.30 | 3.60 | ||
| Dissipation Factor | IEC 60250 | |||
| 100 Hz | 5.0E-3 | 0.18 | ||
| 1 MHz | 0.011 | 0.040 | ||
| Comparative Tracking Index | 600 | -- | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Burning Rate (1.00 mm) | 24 | -- | mm/min | ISO 3795 |
| Flammability Classification | IEC 60695-11-10, -20 | |||
| 0.750 mm | HB | -- | ||
| 1.50 mm | HB | -- |
| Note Message | |
|---|---|
| 1 . | 10°C/min |
| 2 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Matrixx 14A4150 | The Matrixx Group, Inc. | PP, Unspecified | Matrixx |
| RTP 2099 X 126218 D | RTP Company | PLA | RTP |
| ALCOM® TCD PA66 5040 14016 | ALBIS PLASTIC GmbH | Nylon 66 | ALCOM® TCD PA66 |
| Kumho ABS 780F | Korea Kumho Petrochemical Co., Ltd. | ABS | Kumho ABS |
| DOWLEX™ GM 8071G | The Dow Chemical Company | LLDPE | DOWLEX™ |