HiFill® PPS 0334 A
| Category: | PPS , Polyphenylene Sulfide |
| Manufacturer: | Techmer Engineered Solutions |
| Trademark: | HiFill® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ZhK1rr_HiFill-PPS-0334-A.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| HiFill® PPS 0334 A is a Polyphenylene Sulfide (PPS) product. It can be processed by injection molding and is available in North America. Primary characteristic: flame rated. |
| General Information | |
|---|---|
| Features |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 3.43 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.18 mm) | 0.30 | % | ASTM D955 |
| Water Absorption (24 hr) | 0.020 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 100 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Break) | 89.6 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 1.0 | % | ASTM D638 |
| Flexural Modulus | 12400 | MPa | ASTM D790 |
| Flexural Strength | 138 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.18 mm) | 37 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 280 | °C | |
| 1.8 MPa, Unannealed | 266 | °C | |
| CLTE - Flow | 1.6E-5 | cm/cm/°C | ASTM D696 |
| Thermal Conductivity | 1.7 | W/m/K | ASTM C177 |
| RTI Elec (1.50 mm) | 220 | °C | UL 746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+4 to 1.0E+6 | ohms·cm | ASTM D257 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.399 mm | V-0 | ||
| 1.00 mm | 5VA |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 163 | °C | |
| Drying Time | 4.0 | hr | |
| Rear Temperature | 288 to 304 | °C | |
| Middle Temperature | 316 to 343 | °C | |
| Front Temperature | 310 to 332 | °C | |
| Nozzle Temperature | 316 to 332 | °C | |
| Processing (Melt) Temp | 324 to 338 | °C | |
| Mold Temperature | 129 to 163 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Telcar® OBC 4945F | Teknor Apex Company | TPE | Telcar® |
| ARK 2150-40A | Arkadia Plastics, Inc. | TPU, Unspecified | ARK |
| apilon 52® MS 62 | API SpA | TPU-Polyester | apilon 52® |
| Chansieh Phenolic J-361 | Chansieh Enterprises Co., LTD. | Phenolic | Chansieh Phenolic |
| O'Tech OF 8225 | O'Tech Corporation | PVC, Unspecified | O'Tech |