Maxiglas® MG515
| Category: | Acrylic (PMMA) , Polymethyl Methacrylate Acrylic |
| Manufacturer: | Maxiglas Corporation |
| Trademark: | Maxiglas® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Zgxqx7_Maxiglas-MG515.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Maxiglas® is a continuousl mass polymerization acrylic pellet that has outstanding optical properties, excellent weather resistance, uniform color and impact resistance. It has exceptional freedom from war page, cracks, scratches, blisters, voids, foreign matter, and other defects which may affect appearance or serviceability. Applications:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.19 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/3.8 kg) | 15 | g/10 min | ASTM D1238 |
| Water Absorption (24 hr) | 0.30 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (M-Scale) | 90 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | 63.7 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 5.0 | % | ASTM D638 |
| Flexural Modulus | 3140 | MPa | ASTM D790 |
| Flexural Strength | 93.2 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Unnotched Izod Impact | 16 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 90.0 | °C | ASTM D648 |
| Vicat Softening Temperature | 94.0 | °C | ASTM D1525 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Refractive Index | 1.490 | ASTM D542 | |
| Transmittance (3000 µm) | 93.0 | % | ASTM D1003 |
| Haze (3000 µm) | 0.30 | % | ASTM D1003 |
| Additional Information | Nominal Value | Unit | |
|---|---|---|---|
| Foreign Material 1 | < 0.0500 | mm² |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 70.0 to 95.0 | °C | |
| Drying Time | 4.0 | hr | |
| Rear Temperature | 170 to 210 | °C | |
| Middle Temperature | 170 to 210 | °C | |
| Front Temperature | 170 to 210 | °C | |
| Mold Temperature | 30.0 to 50.0 | °C | |
| Injection Pressure | 2.76 to 5.52 | MPa |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 70.0 to 95.0 | °C | |
| Drying Time | 4.0 | hr |
| Note Message | |
|---|---|
| 1 . | Condition: 50g |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Argothane® ST-3850FS-85 | Argotec LLC | TPU, Unspecified | Argothane® |
| Hostalen PP H2483 | LyondellBasell Industries | PP Copolymer | Hostalen PP |
| LNP™ LUBRICOMP™ RAP22 compound | SABIC Innovative Plastics | Nylon 66 | LNP™ LUBRICOMP™ |
| LUVOCOM® 80-7555 VP | Lehmann & Voss & Co. | Acetal (POM) Copolymer | LUVOCOM® |
| POLYCOMPO PE 5000S | POLYCOMPO Co.,Ltd. | HDPE | POLYCOMPO PE |