OmniCarb™ PC220
| Category: | PC , Polycarbonate |
| Manufacturer: | OMNI Plastics, LLC |
| Trademark: | OmniCarb™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ZghXN7_OmniCarb-PC220.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Easy Flow, Flame Resistant Polycarbonate |
| General Information | |
|---|---|
| Features |
|
| UL File Number |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.20 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (300°C/1.2 kg) | 20 | g/10 min | ASTM D1238 |
| Molding Shrinkage | 3.0E-3 to 7.0E-3 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield, 23°C) | 60.7 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 100 | % | ASTM D638 |
| Flexural Modulus | 2280 | MPa | ASTM D790 |
| Flexural Strength | 89.6 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.18 mm) | 640 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 3.18 mm) | 127 | °C | ASTM D648 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.50 mm | V-2 | ||
| 3.00 mm | V-2 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 3.0 to 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Rear Temperature | 249 to 293 | °C | |
| Middle Temperature | 271 to 304 | °C | |
| Front Temperature | 271 to 304 | °C | |
| Nozzle Temperature | 271 to 304 | °C | |
| Processing (Melt) Temp | 271 to 304 | °C | |
| Mold Temperature | 48.9 to 104 | °C | |
| Back Pressure | 0.172 to 0.345 | MPa |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 209E | RTP Company | Nylon, Unspecified | RTP |
| SUPREME HIPS SH 731E | Supreme Petrochem Ltd. | PS (HIPS) | SUPREME HIPS |
| Trademark PE LD2923F | Trademark Plastics Corporation | LDPE | Trademark PE |
| Multi-Flex® TPE A5904 LC | Multibase, A Dow Corning Company | TPE | Multi-Flex® TPE |
| Crastin® LW9330 NC010 | DuPont Performance Polymers | PBT | Crastin® |