Generic AES
| Category: | AES , Acrylonitrile Ethylene Styrene |
| Manufacturer: | Generic |
| Trademark: | Generic |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Zg3ZpD_Generic-AES.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
This data represents typical values that have been calculated from all products classified as: Generic AES This information is provided for comparative purposes only. |
| General Information |
|---|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.04 - 1.05 | g/cm³ | ASTM D792 |
| 23°C | 1.04 - 1.07 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) | |||
| 220°C/10.0 kg | 5.0 - 35 | g/10 min | ASTM D1238 |
| 220°C/10.0 kg | 5.0 - 18 | g/10 min | ISO 1133 |
| Melt Volume-Flow Rate (MVR) (220°C/2.16 kg) | 8.13 - 51.9 | cm³/10min | ISO 1133 |
| Molding Shrinkage | |||
| Flow : 23°C | 0.55 - 0.70 | % | ASTM D955 |
| 23°C | 0.50 - 0.70 | % | ISO 294-4 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness | |||
| 23°C | 93 - 112 | ASTM D785 | |
| 23°C | 100 - 108 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 1970 - 2360 | MPa | ISO 527-2 |
| Tensile Strength | |||
| Yield, 23°C | 48.8 - 53.9 | MPa | ASTM D638 |
| Yield, 23°C | 38.0 - 51.6 | MPa | ISO 527-2 |
| 23°C | 37.0 - 50.0 | MPa | ISO 527-2 |
| Flexural Modulus | |||
| 23°C | 2000 - 2450 | MPa | ASTM D790 |
| 23°C | 2000 - 2720 | MPa | ISO 178 |
| Flexural Strength | |||
| 23°C | 55.0 - 90.2 | MPa | ASTM D790 |
| 23°C | 54.7 - 78.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 6.0 - 32 | kJ/m² | ISO 179 |
| Notched Izod Impact (23°C) | 110 - 210 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, not annealed | 84.6 - 90.6 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 71.7 - 89.2 | °C | ISO 75-2/A |
| CLTE - Flow | 8.0E-5 - 9.0E-5 | cm/cm/°C | ISO 11359-2 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 - 88.3 | °C | |
| Drying Time | 3.0 - 3.5 | hr | |
| Rear Temperature | 188 - 250 | °C | |
| Middle Temperature | 214 - 250 | °C | |
| Front Temperature | 209 - 254 | °C | |
| Nozzle Temperature | 210 - 247 | °C | |
| Processing (Melt) Temp | 215 - 260 | °C | |
| Mold Temperature | 55.0 - 65.0 | °C | |
| Back Pressure | 0.776 - 10.0 | MPa | |
| Screw Speed | 45 - 75 | rpm |
| Injection instructions |
|---|
| This data represents typical values that have been calculated from all products classified as: Generic AESThis information is provided for comparative purposes only. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Ultraform® N 2650 Z2 | BASF Corporation | Acetal (POM) Copolymer | Ultraform® |
| Centrex® ST4800 | Network Polymers, Inc. | ASA+TPE | Centrex® |
| GERMAMID 6 MF 30 HSZ | Kunststoff-Kontor-Hamburg GmbH | Nylon 6 | GERMAMID |
| Escorene™ Ultra UL 00218CC3 | ExxonMobil Chemical | EVA | Escorene™ Ultra |
| Karina GRAY COLOR CONCENTRATE 18/367-FC-LMP | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |