TEKAFIN™ PB50FR
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | Mando Advanced Materials Co., Ltd. |
| Trademark: | TEKAFIN™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Zf4sFT_TEKAFIN-PB50FR.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PB50FR is a unreinforced flame retardant PP. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.01 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 1.4 to 1.6 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Break) | 28.4 | MPa | ASTM D638 |
| Tensile Elongation 2(Break) | 50 | % | ASTM D638 |
| Flexural Modulus 3 | 1770 | MPa | ASTM D790 |
| Flexural Strength 4 | 42.2 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.18 mm) | 61 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed) | 130 | °C | ASTM D648 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | V-0 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 70.0 to 80.0 | °C | |
| Drying Time | 3.0 to 4.0 | hr | |
| Rear Temperature | 190 to 210 | °C | |
| Middle Temperature | 200 to 230 | °C | |
| Front Temperature | 200 to 230 | °C | |
| Nozzle Temperature | 210 to 230 | °C | |
| Processing (Melt) Temp | 210 to 230 | °C | |
| Mold Temperature | 40.0 to 60.0 | °C |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| 3 . | 3.0 mm/min |
| 4 . | 3.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Small Boss RPVC004 | Tongxiang Small Boss Special Plastic Products Co., Ltd. | PVC, Rigid | Small Boss |
| Tufpet PBT N2800 | Mitsubishi Rayon America Inc. | PBT | Tufpet |
| LNP™ THERMOCOMP™ WF004 compound | SABIC Innovative Plastics | PBT | LNP™ THERMOCOMP™ |
| Exceed™ 1012HA | ExxonMobil Chemical | mPE | Exceed™ |
| Durethan® AKV 35 XTS1 901510 | LANXESS GmbH | Nylon 66 | Durethan® |