| Mineral reinforced PP Modified, Heat resistant |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.08 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 5.0 | g/10 min | ISO 1133 |
| Molding Shrinkage | ISO 294-4 | ||
| Across Flow | 0.90 to 1.1 | % | |
| Flow | 0.90 to 1.1 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | 22.0 | MPa | ISO 527-2 |
| Tensile Strain (Yield) | 6.0 | % | ISO 527-2 |
| Flexural Modulus (23°C) | 1900 | MPa | ISO 178 |
| Flexural Stress | 40.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | ||
| -40°C | 2.5 | kJ/m² | |
| -30°C | 3.5 | kJ/m² | |
| -20°C | 5.0 | kJ/m² | |
| 23°C | 15 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179 | ||
| -40°C | 32 | kJ/m² | |
| -30°C | No Break | ||
| -20°C | No Break | ||
| 23°C | No Break |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 1 | |||
| 0.45 MPa, Unannealed | 125 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 70.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | |||
| -- | 149 | °C | ISO 306/A50 |
| -- | 73.0 | °C | ISO 306/B50 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.60 mm) | HB | UL 94 | |
| Glow Wire Ignition Temperature (2.00 mm) | 750 | °C | IEC 60695-2-13 |
| Note Message | |
|---|---|
| 1 . | 120°C/hr |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Maxelast® P3672 | Nantong Polymax Elastomer Technology, Co., Ltd | TPE | Maxelast® |
| POLYLAN AG15A1 | POLYMA Kunststoff GmbH & Co. KG | ABS | POLYLAN |
| Pro PP-HO-HF-30T | Pro Polymers | PP Homopolymer | Pro-Comp™ |
| TECHNYL® A 216 S40 NATURAL | Solvay Engineering Plastics | Nylon 66 | TECHNYL® A |
| Glastic® CBC | Glastic Corporation | Polyester, TS | Glastic® |