EcoPaXX® Q-X07207
| Category: | Nylon 410 , Polyamide 410 |
| Manufacturer: | DSM Engineering Plastics |
| Trademark: | EcoPaXX® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ZeUI5m_EcoPaXX-Q-X07207.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
EcoPaXX® Q-X07207 is a Polyamide 410 (Nylon 410) material. It is available in Asia Pacific, Europe, or North America. Important attributes of EcoPaXX® Q-X07207 are:
|
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.05 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | |||
| Across Flow | 1.8 | -- | % | |
| Flow | 2.8 | -- | % | |
| Water Absorption (Equilibrium, 23°C, 50% RH) | 1.7 | -- | % | ISO 62 |
| Calculated Bio-based Carbon Content | 56 | -- | % | ASTM D6866 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 2000 | 940 | MPa | ISO 527-2 |
| Tensile Stress (Yield) | 50.0 | 35.0 | MPa | ISO 527-2 |
| Tensile Strain (Yield) | 6.0 | 20 | % | ISO 527-2 |
| Nominal Tensile Strain at Break | 30 | > 50 | % | ISO 527-2 |
| Flexural Modulus | 1750 | 950 | MPa | ISO 178 |
| Flexural Stress | 70.0 | 40.0 | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -30°C | 20 | -- | kJ/m² | |
| 23°C | 65 | 75 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -30°C | No Break | -- | ||
| 23°C | No Break | No Break |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, Unannealed | 140 | -- | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 75.0 | -- | °C | ISO 75-2/A |
| Melting Temperature 1 | 250 | -- | °C | ISO 11357-3 |
| CLTE | ISO 11359-2 | |||
| Flow | 1.4E-4 | -- | cm/cm/°C | |
| Transverse | 1.2E-4 | -- | cm/cm/°C |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Volume Resistivity | > 1.0E+15 | 5.0E+14 | ohms·cm | IEC 60093 |
| Electric Strength | 35 | 33 | kV/mm | IEC 60243-1 |
| Comparative Tracking Index | -- | 600 | V | IEC 60112 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 4.0 to 8.0 | hr | |
| Rear Temperature | 250 to 270 | °C | |
| Middle Temperature | 260 to 280 | °C | |
| Front Temperature | 270 to 290 | °C | |
| Nozzle Temperature | 270 to 300 | °C | |
| Processing (Melt) Temp | 270 to 300 | °C | |
| Mold Temperature | 60.0 to 100 | °C | |
| Injection Rate | Moderate-Fast | ||
| Back Pressure | 3.00 to 10.0 | MPa | |
| Screw Compression Ratio | 2.5:1.0 |
| Note Message | |
|---|---|
| 1 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TOTAL Polypropylene PPR 7450HC | TOTAL Refining & Chemicals | PP Random Copolymer | TOTAL Polypropylene |
| Electrafil® PC 04005 FR BK | Techmer Engineered Solutions | PC | Electrafil® |
| Kemcor LD 9151 | Qenos Pty Ltd | LDPE | Kemcor |
| Kepital® FC2010DX | KEP Americas | Acetal (POM) Copolymer | Kepital® |
| Sylvin 8482-75 Natural | Sylvin Technologies Incorporated | PVC+NBR | Sylvin |