Jamplast JPLGABSI
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | Jamplast, Inc. |
| Trademark: | Jamplast |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Zchik2_Jamplast-JPLGABSI.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Jamplast ABS resins are thermoplastic materials which provide an excellent balance of processability, impact resistance and heat resistance as imparted by the various polymer compositions. Jamplast ABS resins are available in a wide range of melt flow rates, impact strength and heat resistance for both high and low gloss applications manufactured by injection molding, sheet or profile extrusion and thermoforming processes. Automotive Jamplast ABS resins offer a wide range of gloss, viscosity, impact strength and heat properties for use in numerous automotive applications. Melt flow rates from 1 to 12 g/10 min, impact strengths from 2.5 to 12 ft-lb/in and heat distortion temperatures from 165°F to 190°F are available. Available primarily as natural plus concentrates, Jamplast ABS resins are used in a wide variety of automotive applications including structural instrument panels, consoles, pillars, and exterior trim parts requiring painting and plating. Jamplast JPLGABSI ABS resin is a high flow, low gloss ABS resin often used in door panels, consoles, and various interior trim. |
| General Information | |
|---|---|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.04 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/3.8 kg) | 6.0 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 0.40 to 0.70 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1 | 1790 | MPa | ASTM D638 |
| Tensile Strength 2(Yield) | 41.4 | MPa | ASTM D638 |
| Tensile Elongation 3(Yield) | 3.0 | % | ASTM D638 |
| Flexural Modulus 4 | 2070 | MPa | ASTM D790 |
| Flexural Strength 5 | 58.6 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact 6 | ASTM D256 | ||
| -18°C, 3.18 mm | 80 | J/m | |
| 23°C, 3.18 mm | 160 | J/m | |
| Instrumented Dart Impact 7 | ASTM D3763 | ||
| 23°C, 3.18 mm, Peak Energy | 32.8 | J | |
| 23°C, 3.18 mm, Total Energy | 42.9 | J |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed, 3.18 mm | 90.6 | °C | |
| 1.8 MPa, Unannealed, 3.18 mm | 76.7 | °C | |
| Vicat Softening Temperature | 104 | °C | ASTM D1525 |
| CLTE - Flow | 7.4E-5 | cm/cm/°C | ASTM D696 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 to 85.0 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Suggested Max Moisture | 0.10 | % | |
| Processing (Melt) Temp | 232 to 246 | °C | |
| Mold Temperature | 26.7 to 48.9 | °C | |
| Back Pressure | 0.345 to 3.45 | MPa | |
| Clamp Tonnage | 2.8 to 4.1 | kN/cm² | |
| Screw L/D Ratio | 20.0:1.0 | ||
| Screw Compression Ratio | 1.5:1.0 to 3.5:1.0 |
| Note Message | |
|---|---|
| 1 . | Type I, 51 mm/min |
| 2 . | Type I, 51 mm/min |
| 3 . | Type I, 51 mm/min |
| 4 . | Type I, 1.3 mm/min |
| 5 . | Type I, 1.3 mm/min |
| 6 . | 0.25 mm Notch Depth |
| 7 . | 3.39 m/sec |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| MAZMID B 150 FV10 EV20 | Mazzaferro Indústria e Comércio de Polímeros e Fibras Ltda. | Nylon 6 | MAZMID B |
| SILVER® SA-3698 | Guangdong Silver Age Sci & Tech. Co., Ltd | TPE | SILVER® |
| ADMER™ NF528A | Mitsui Chemicals America, Inc. | PE, Unspecified | ADMER™ |
| Chiao Fu PA66 MD212G43 NAT | Chiao Fu Enterprises Co., Ltd. | Nylon 66 | Chiao Fu PA66 |
| InnoClear™ VA-273 | Innovative Polymers, Inc. | TSU | InnoClear™ |