Order Products : sales@su-jiao.com
Medalist® MD-105
| Category: | TPE , Thermoplastic Elastomer |
| Manufacturer: | Teknor Apex Company |
| Trademark: | Medalist® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ZbaAfs_Medalist-MD-105.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| This compound is designed for medical and healthcare applications requiring a soft, gel-like material. |
| General Information | |
|---|---|
| Uses |
|
| Agency Ratings |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.878 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 15 | g/10 min | ASTM D1238 |
| Molding Shrinkage | ASTM D955 | ||
| Flow | 2.8 | % | ASTM D955 |
| Transverse flow | 2.4 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore A) | 18 | ASTM D2240 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ASTM D412 | ||
| 100% strain | 0.345 | MPa | ASTM D412 |
| 200% strain | 0.483 | MPa | ASTM D412 |
| 300% strain | 0.689 | MPa | ASTM D412 |
| Tensile Strength (Break) | 4.14 | MPa | ASTM D412 |
| Tensile Elongation (Break) | 600 | % | ASTM D412 |
| Tear Strength | 17.5 | kN/m | ASTM D624 |
| Compression Set (23°C, 22 hr) | 23 | % | ASTM D395 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Rear Temperature | 138 - 149 | °C | |
| Middle Temperature | 149 - 160 | °C | |
| Front Temperature | 160 - 171 | °C | |
| Nozzle Temperature | 171 - 182 | °C | |
| Processing (Melt) Temp | 171 - 182 | °C | |
| Mold Temperature | 21.1 - 37.8 | °C | |
| Injection Pressure | 1.38 - 5.52 | MPa | |
| Back Pressure | 0.172 - 0.689 | MPa | |
| Screw Speed | 50 - 100 | rpm | |
| Cushion | 3.81 - 25.4 | mm |
| Injection instructions |
|---|
| Drying is not necessary. However, if moisture is a problem, dry the pellets for 2 to 4 hours at 150°F (65°C). |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| megol® DP1741 85 | API SpA | SEBS | megol® |
| NuSil R-3900 | NuSil Technology | Silicone | NuSil |
| Nypol® PA B3 G63 HS PRTA012 NT380 | Petropol Industry and Trade of Polymers LTDA | Nylon 6 | Nypol® PA |
| Dynaprene® SE9030A | Nantex Industry Co., Ltd. | TPE | Dynaprene® |
| Sylvin 9604-95C Clear 896 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |