Grupo IDESA HIPS HI-760-L-01
| Category: | SBC , Styrene Butadiene Block Copolymer |
| Manufacturer: | Grupo IDESA, S.A. de C.V. |
| Trademark: | Grupo IDESA HIPS |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Zaqna8_Grupo-IDESA-HIPS-HI-760-L-01.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| High Impact Styrene-Butadiene Copolymer in form of pellet, in white color and easy molding. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melt Mass-Flow Rate (MFR) (200°C/5.0 kg) | 5.5 | g/10 min | ASTM D1238 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | ASTM D638 | ||
| Yield | 22.6 | MPa | ASTM D638 |
| Fracture | 25.0 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 30 | % | ASTM D638 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 100 | J/m | ASTM D256 |
| Additional Information |
|---|
| The value listed as Tensile Elongation @ Break, ASTM D638, was tested in accordance with MP-722 test method.Melt Mass-Flow Rate, MP-720, 200°C/5.0 kg: 4 to 7 g/10 minNotched Izod Impact, MP-721: 9 to 11.5 kg-cm/cmTensile Strength @ Yield, MP-722: 200 to 260 kg/cm²Tensile Strength @ Break, MP-722: 210 to 300 kg/cm²Pellet Size. MP-725: 3 mm maxPellet>3=<20 mm: 0.99% maxPellet>20 mm: 0.01% max |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Telcar® TL-1424A | Teknor Apex Company | TPE | Telcar® |
| Toughblend® PA66-1900 | Colour Image Plastic Compound Sdn. Bhd. (CIPC) | Nylon 6 | Toughblend® |
| TRISTAR® PC-30GFR | Polymer Technology and Services, LLC | PC | TRISTAR® |
| EOS PA 2200 Balance 1.0 | EOS GmbH | Nylon 12 | EOS |
| Geon™ Vinyl Rigid Molding M5100 | PolyOne Corporation | PVC, Rigid | Geon™ Vinyl Rigid Molding |