FINGERPRINT™ DFDD-7525 NT
| Category: | MDPE , Polyethylene Resin |
| Manufacturer: | The Dow Chemical Company |
| Trademark: | FINGERPRINT™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ZWcK42_FINGERPRINTDFDD7525NT.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
FINGERPRINT™ DFDD-7525 NT is a medium density polyethylene resin designed for use in thin-wall microirrigation tape applications. This product was designed to offer good profile extrusion processing characteristics coupled with great application performance attributes such as toughness, burst strength and environmental stress crack resistance. Main Characteristics:
Industrial Standards Compliance:
|
| General Information | |
|---|---|
| Agency Ratings |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.940 | g/cm³ | ASTM D972 |
| Melt Mass-Flow Rate (MFR) | ASTM D1238 | ||
| 190°C/2.16 kg | > 0.15 | g/10 min | ASTM D1238 |
| 190°C/21.6 kg | 20 | g/10 min | ASTM D1238 |
| Environmental Stress-Cracking Resistance 1(F0) | > 2000 | hr | ASTM D1693A |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness 2(Shore D) | 55 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 3 | ASTM D638 | ||
| Yield | 26.2 | MPa | ASTM D638 |
| Fracture | 30.0 | MPa | ASTM D638 |
| Tensile Elongation 4(Break) | > 800 | % | ASTM D638 |
| Flexural Modulus 5 | 689 | MPa | ASTM D790 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature 6 | < -100 | °C | ASTM D746A |
| Vicat Softening Temperature | 116 | °C | ASTM D1525 |
| Melting Temperature (DSC) | 125 | °C | Internal method |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 220 - 250 | °C |
| Note Message | |
|---|---|
| 1 . | Prepare the compression molded fitting according to ASTM D 1928 procedure C. Attributes will vary with molding conditions and aging time. |
| 2 . | Prepare the compression molded fitting according to ASTM D 1928 procedure C. Attributes will vary with molding conditions and aging time. |
| 3 . | Prepare the compression molded fitting according to ASTM D 1928 procedure C. Attributes will vary with molding conditions and aging time. |
| 4 . | Prepare the compression molded fitting according to ASTM D 1928 procedure C. Attributes will vary with molding conditions and aging time. |
| 5 . | Prepare the compression molded fitting according to ASTM D 1928 procedure C. Attributes will vary with molding conditions and aging time. |
| 6 . | Prepare the compression molded fitting according to ASTM D 1928 procedure C. Attributes will vary with molding conditions and aging time. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Michimid K4200GF33-01 | API Polymers, Inc. | Nylon 66 | Michimid |
| TechnoPet 3310 | TechnoCompound GmbH | PET | TechnoPet |
| Bayflex® XGT-2 (50% BaSO4) | Covestro - PUR | PUR-MDI | Bayflex® |
| Panlite® G-3420R | TEIJIN LIMITED | PC | Panlite® |
| Plasmer 7065B/8901 | HYUNDAI EP Co., Ltd. | TPE | Plasmer |