PRIMACOR™ 3330

Category:	EAA , Copolymer
Manufacturer:	The Dow Chemical Company
Trademark:	PRIMACOR™
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	ZWH8MQ_PRIMACOR-3330.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

WECHAT

Message

PRIMACOR™3330 copolymer is an ethylene acrylic acid copolymer suitable for extrusion coating and extrusion lamination applications.

PRIMACOR 3330 copolymer is specially used as binder resin or sealant layer in extrusion and co-extrusion coating and extrusion lamination. PRIMACOR 3330 copolymer has the following characteristics:

Excellent adhesion with metal, paper and PE substrates

Excellent heat sealing performance and heat adhesion performance

Excellent toughness

excellent grease resistance

Insensitive to moisture

Application field:

Soft packaging composites

plastic pipe composite material

Meet the following regulatory requirements:

U.S. Food and Drug Administration (U.S. FDA)21 CFR 177.1310(a)(1)

European Union (EU) No 10/2011

Please refer to the regulations for detailed information

General Information
Agency Ratings	FDA 21 CFR 177.1310 (a) 1 Europe No 10/2011
Forms	Particle
Processing Method	Extrusion coating

Physical	Nominal Value	Unit	Test Method
Specific Gravity	0.932	g/cm³	ASTM D792, ISO 1183
Melt Mass-Flow Rate (MFR) ¹(190°C/2.16 kg)	5.8	g/10 min	ASTM D1238, ISO 1133
Comonomer Content ²	6.5	%	Internal method

Mechanical	Nominal Value	Unit	Test Method
Tensile Strength			ASTM D638, ISO 527-2
Yield, molding	8.34	MPa	ASTM D638, ISO 527-2
Fracture, molding	17.4	MPa	ASTM D638, ISO 527-2
Tensile Elongation (Break, Compression Molded)	520	%	ASTM D638, ISO 527-2

Films	Nominal Value	Unit	Test Method
Seal Initiation Temperature ³	92.8	°C	Internal method
Water Vapor Transmission Rate (38°C, 90% RH)	0.40	g·mm/m²/atm/24 hr	DIN 53122/2

Thermal	Nominal Value	Unit	Test Method
Vicat Softening Temperature	85.0	°C	ASTM D1525, ISO 306
Melting Temperature (DSC)	100	°C	Internal method

Extrusion	Nominal Value	Unit	Test Method
Melt Temperature	260 - 290	°C
Neck-in (288°C, 25.4 µm)	50.8	mm	Internal method
Minimum coating thickness	20	µm	Internal method
Minimum coating weight	20	g/m²	Internal method

Extrusion instructions
挤出涂层薄膜的制造条件：用于处理此树脂的设备应由耐腐蚀材料制成。建议模具和适配器采用不锈钢和/或双面镀铬或镀镍。螺杆尺寸：3.5 英寸 (89 mm)；30:1 L/D 模具：30 英寸模具切边至 24 英寸模具间隙：20 密尔 (0.508 mm) 熔体温度：550 °F (288 °C) 输出：250 磅/小时气隙：6 英寸 (152 mm)

Note Message
1 .	As measured during production.
2 .	The comonomer content measured by Dow attribute method has the same accuracy as ASTM D 4094.
3 .	25g/m coating at 290°C set temperature.

Resin Grade	Manufacturer	Category	Trademark
Wellamid® 42LN2-N	Wellman Engineering Resins	Nylon 6	Wellamid®
Cri-Line LC-815	Cri-Tech, Inc.	Fluorelastomer	Cri-Line
Estane® 58630 TPU	Lubrizol Advanced Materials, Inc.	TPU-Polyether	Estane®
Karina NATURAL PVC COMPOUND -E V-150 LT	Karina Ind. e Com. de Plásticos Ltda	PVC, Unspecified	Karina
LUVOCOM® 1104-VAP 10	Lehmann & Voss & Co.	PEK	LUVOCOM®