Makroblend® UT4045 G
| Category: | PC+PBT , Polycarbonate + PBT |
| Manufacturer: | Covestro - Polycarbonates |
| Trademark: | Makroblend® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ZWE8QO_Makroblend-UT4045-G.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| (PC+PBT)-blend, 20% Glass fiber reinforced, easy release, injection molding. Makroblend UT4045G offers a high stiffness, excellent chemical resistance, good flowability and exceptional dimensional stability. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 1.40 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (260°C/5.0 kg) | 30.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage | ISO 2577 | ||
| Across Flow 1 | 0.20 to 0.60 | % | |
| Across Flow : 90°C, 1 hr | < 0.10 | % | |
| Flow 2 | 0.20 to 0.60 | % | |
| Flow : 90°C, 1 hr | < 0.10 | % | |
| Across Flow : 260°C, 3.00 mm 3 | 0.50 to 0.70 | % | |
| Flow : 260°C, 3.00 mm 4 | 0.20 to 0.40 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Ball Indentation Hardness | 90.0 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 6500 | MPa | ISO 527-2/1 |
| Tensile Stress | ISO 527-2/5 | ||
| Yield, 23°C | 100 | MPa | |
| Break, 23°C | 100 | MPa | |
| Tensile Strain | ISO 527-2/5 | ||
| Yield, 23°C | 3.0 | % | |
| Break, 23°C | 3.0 | % | |
| Nominal Tensile Strain at Break (23°C) | 3.0 | % | ISO 527-2/5 |
| Flexural Modulus 5(23°C) | 6100 | MPa | ISO 178 |
| Flexural Stress 6(23°C) | 160 | MPa | ISO 178 |
| Flexural Strain at Flexural Strength 7(23°C) | 3.0 | % | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -30°C | 40 | kJ/m² | |
| 23°C | 45 | kJ/m² | |
| Notched Izod Impact Strength | ISO 180/A | ||
| -30°C | 6.0 | kJ/m² | |
| 23°C | 6.0 | kJ/m² | |
| Unnotched Izod Impact Strength | ISO 180 | ||
| -30°C | 35 | kJ/m² | |
| 23°C | 40 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 130 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 110 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 140 | °C | ISO 306/B120 |
| Note Message | |
|---|---|
| 1 . | 600 bar |
| 2 . | 600 bar |
| 3 . | 150x105x3 mm, 80°C MT, 600 bar |
| 4 . | 150x105x3 mm, 80°C MT, 600 bar |
| 5 . | 2.0 mm/min |
| 6 . | 2.0 mm/min |
| 7 . | 2 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| POPELEN A-354 | Lotte Chemical Corporation | PP Impact Copolymer | POPELEN |
| SABIC® PPcompound 5450 | Saudi Basic Industries Corporation (SABIC) | PP, Unspecified | SABIC® PPcompound |
| SEMICOSIL® 911 A/B | Wacker Chemie AG | Silicone | SEMICOSIL® |
| CALIBRE™ 201-6 | Trinseo | PC | CALIBRE™ |
| Elastron® G G100.A70.N | Elastron USA, Inc. | SEBS | Elastron® G |