Tufel® II 94505

Category:	Silicone , Silicone
Manufacturer:	Momentive Performance Materials Inc.
Trademark:	Tufel® II
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	ZTo05g_Tufel-II-94505.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

Message
TUFEL* II Silicone Rubber Compounds 94405, 94505, 94605, and 94705 are 40-70 durometer low volatile fast-cure addition cured silicone elastomers for molding. They may be used by themselves or blended to intermediate durometers. Applications include fabricated molding that require short cycle time, deep section cures, and parts with low extractable requirements. Key Features and Benefits LV Bases Minimize Post Cure Times Totally Peroxide-Free Cure System Significant Reduction in Molding cycle Times Lower Molding Temperature Range (150-166C) (300-330F) Superior Mixed Shelf Life High Tear Strength Tight Surface Cure Non-blooming Translucency

Message

TUFEL* II Silicone Rubber Compounds 94405, 94505, 94605, and 94705 are 40-70 durometer low volatile fast-cure addition cured silicone elastomers for molding. They may be used by themselves or blended to intermediate durometers. Applications include fabricated molding that require short cycle time, deep section cures, and parts with low extractable requirements.

Key Features and Benefits

LV Bases Minimize Post Cure Times

Totally Peroxide-Free Cure System

Significant Reduction in Molding cycle Times

Lower Molding Temperature Range (150-166C) (300-330F)

Superior Mixed Shelf Life

High Tear Strength

Tight Surface Cure

Non-blooming

Translucency

General Information
Features	Fast Cure Fast Molding Cycle Good Tear Strength Low Extractables Non-Blooming
Appearance	Translucent
Processing Method	Injection Molding

Hardness	Nominal Value		Test Method
Durometer Hardness (Shore A)	47		ASTM D2240

Elastomers	Nominal Value	Unit	Test Method
Tensile Stress (100% Strain)	1.20	MPa	ASTM D412
Tensile Strength	9.10	MPa	ASTM D412
Tensile Elongation (Break)	930	%	ASTM D412
Tear Strength ¹	43.9	kN/m	ASTM D624

Uncured Properties	Nominal Value	Unit
Density	1.15	g/cm³
Curing Time (177°C)	0.17	hr

Note Message
1 .	Die B

Resin Grade	Manufacturer	Category	Trademark
Sarlink® TPV 4765B40	Teknor Apex Company	TPV	Sarlink® TPV
ALCUDIA® EVA PA-444	REPSOL	EVA	ALCUDIA® EVA
Latimass 62-01 D025	LATI S.p.A.	Nylon 6	Latimass
Plenco 07321 (Compression)	Plastics Engineering Co.	Phenolic	Plenco
Hifax TYC 381P 1646	LyondellBasell Industries	PP Copolymer	Hifax