DOWLEX™ 2032
| Category: | LLDPE , Polyethylene Resin |
| Manufacturer: | The Dow Chemical Company |
| Trademark: | DOWLEX™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ZTV10A_DOWLEX-2032.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
| General Information | |
|---|---|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.926 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 2.0 | g/10 min | ASTM D1238 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 25 | µm | |
| Film Puncture Resistance (25 µm) | 18.2 | J/cm³ | Internal method |
| Film strength | ASTM D882 | ||
| MD : 25 µm | 255 | J/cm³ | ASTM D882 |
| TD : 25 µm | 228 | J/cm³ | ASTM D882 |
| Tensile Strength | ASTM D882 | ||
| MD : Yield, 25 µm | 12.0 | MPa | ASTM D882 |
| TD : Yield, 25 µm | 11.9 | MPa | ASTM D882 |
| MD : Break, 25 µm | 64.3 | MPa | ASTM D882 |
| TD : Break, 25 µm | 35.2 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : Break, 25 µm | 470 | % | ASTM D882 |
| TD : Break, 25 µm | 680 | % | ASTM D882 |
| Dart Drop Impact (25 µm) | 120 | g | ASTM D1709A |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 25 µm | 320 | g | ASTM D1922 |
| TD : 25 µm | 680 | g | ASTM D1922 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 109 | °C | ASTM D1525 |
| Melting Temperature (DSC) | 124 | °C | Internal method |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°, 25.4 µm) | 91 | ASTM D2457 | |
| Haze (25.4 µm) | 2.1 | % | ASTM D1003 |
| Extrusion instructions |
|---|
| 铸造薄膜的制造条件： 螺杆尺寸：2 英寸 (51 mm)；30:1 L/D 螺杆尺寸：2.5 英寸 (63.5 mm)；30:1 L/D 螺杆尺寸：2.5 英寸 (63.5 mm)；30:1 L/D 螺杆尺寸：2.5 英寸 (63.5 mm)；30:1 L/D 螺杆尺寸：2 英寸 (51 mm)；30:1 L/D 模具间隙：25 密尔 (0.6 mm) 冷却辊温度：70°F (21°C) 熔体温度：525°F (274°C) 生产线速度：600 fpm（183 米/分） |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Ultraform® S 2320 003 UNC Q600 | BASF Corporation | Acetal (POM) Copolymer | Ultraform® |
| Cheng Yu N6GV2 | Cheng Yu Plastic Company Limited | Nylon 6 | Cheng Yu |
| KOPA® KN135G33CCHS | Kolon Plastics, Inc. | Nylon 6 | KOPA® |
| LNP™ COLORCOMP™ EX14001 compound | SABIC Innovative Plastics Europe | PEI | LNP™ COLORCOMP™ |
| Panlite® LN-2250Y | TEIJIN LIMITED | PC | Panlite® |