PA 66, 30 % glass fibers, injection molding, heat-aging stabilized, hydrolysis stabilized

General Information
Filler / Reinforcement	Glass fiber reinforced material, 30% filler by weight
Additive	heat stabilizer
Features	Good heat aging resistance Excellent appearance
Agency Ratings	EC 1907/2006 (REACH)
Processing Method	Injection molding

Physical	Dry	Conditioned	Unit	Test Method
Density (23°C)	1.36	--	g/cm³	ISO 1183
Apparent Density	0.70	--	g/cm³	ISO 60
Molding Shrinkage				ISO 294-4
Vertical flow direction : 290°C, 2.00mm ¹	0.94	--	%	ISO 294-4
Vertical flow direction : 120°C, 2 hours, 2.00mm ²	0.12	--	%	ISO 294-4
Flow direction : 290°C, 2.00mm ³	0.44	--	%	ISO 294-4
Flow direction : 120°C, 2 hours, 2.00mm ⁴	0.060	--	%	ISO 294-4
Water Absorption				ISO 62
Saturated, 23°C	5.5	--	%	ISO 62
Equilibrium, 23°C, 50% RH	2.0	--	%	ISO 62

Hardness	Dry	Conditioned	Unit	Test Method
Ball Indentation Hardness	205	105	MPa	ISO 2039-1

Mechanical	Dry	Conditioned	Unit	Test Method
Tensile Modulus
23°C	9430	5930	MPa	ASTM D638
23°C	9700	6100	MPa	ISO 527-2/1
Tensile Strength
Fracture, 23°C	175	117	MPa	ASTM D638
Fracture, 23°C	180	120	MPa	ISO 527-2/5
Tensile Elongation
Fracture, 23°C	4.0	8.0	%	ASTM D638
Fracture, 23°C	3.5	8.0	%	ISO 527-2/5
Flexural Modulus
23°C	8620	5410	MPa	ASTM D790
23°C ⁵	8600	5400	MPa	ISO 178/A
Flexural Strength
23°C	281	181	MPa	ASTM D790
3.5% strain ⁶	265	150	MPa	ISO 178/A
23°C ⁷	280	180	MPa	ISO 178
Flexural Strain at Flexural Strength ⁸(23°C)	4.0	6.5	%

Flammability	Dry	Conditioned	Unit	Test Method
Burning Behavior ⁹(> 1.00 mm)	passed	--		ISO 3795

Additional Information	Dry	Conditioned		Test Method
ISO Shortname	PA 66, GHWR, 14-100, GF30	--		ISO 1874

Injection	Dry	Unit	Test Method
Residual Moisture Content	0.030 - 0.12	%	Karl Fisher

Films	Dry	Conditioned	Unit	Test Method
Film Puncture Energy				ISO 6603-2
-- ¹⁰	1.90	--	J	ISO 6603-2
-- ¹¹	3.10	4.70	J	ISO 6603-2
Film Puncture Force				ISO 6603-2
-- ¹²	776	--	N	ISO 6603-2
-- ¹³	896	1070	N	ISO 6603-2

Impact	Dry	Conditioned	Unit	Test Method
Charpy Notched Impact Strength				ISO 179/1eA
-40°C	< 10	< 10	kJ/m²	ISO 179/1eA
-30°C	< 10	< 10	kJ/m²	ISO 179/1eA
23°C	10	20	kJ/m²	ISO 179/1eA
Charpy Unnotched Impact Strength				ISO 179/1eU
-30°C	65	75	kJ/m²	ISO 179/1eU
23°C	75	85	kJ/m²	ISO 179/1eU
Notched Izod Impact				ISO 180/1A
-40°C	< 10	< 10	kJ/m²	ISO 180/1A
-30°C	< 10	< 10	kJ/m²	ISO 180/1A
Unnotched Izod Impact Strength				ISO 180/1U
-30°C	60	--	kJ/m²	ISO 180/1U
23°C	70	--	kJ/m²	ISO 180/1U

Thermal	Dry	Conditioned	Unit	Test Method
Heat Deflection Temperature
0.45 MPa, not annealed	250	--	°C	ISO 75-2/B
1.8 MPa, not annealed	245	--	°C	ISO 75-2/A
8.0 MPa, not annealed	125	--	°C	ISO 75-2/C
Vicat Softening Temperature
--	> 230	--	°C	ISO 306/B50
--	254	--	°C	ISO 306/B120
Melting Temperature ¹⁴	262	--	°C	ISO 11357-3
Linear thermal expansion coefficient				ISO 11359-2
Flow : 23 to 55°C	3.0E-5	--	cm/cm/°C	ISO 11359-2
Lateral : 23 to 55°C	9.0E-5	--	cm/cm/°C	ISO 11359-2

Electrical	Dry	Conditioned	Unit	Test Method
Surface Resistivity	1.0E+15	1.0E+13	ohms	IEC 60093
Volume Resistivity (23°C)	1.0E+15	1.0E+11	ohms·cm	IEC 60093
Dielectric Strength (23°C, 1.00 mm)	35	30	kV/mm	IEC 60243-1
Relative Permittivity				IEC 60250
23°C, 100 Hz	4.00	12.0		IEC 60250
23°C, 1 MHz	3.60	4.50		IEC 60250
Dissipation Factor				IEC 60250
23°C, 100 Hz	8.0E-3	0.30		IEC 60250
23°C, 1 MHz	0.016	0.090		IEC 60250
Comparative Tracking Index (Solution A)	450	--	V	IEC 60112

Flammability	Dry	Conditioned	Unit	Test Method
Flame Rating				UL 94
1.60 mm	HB	--		UL 94
3.20 mm	HB	--		UL 94
Glow Wire Flammability Index (2.00 mm)	650	--	°C	IEC 60695-2-12
Oxygen Index ¹⁵	26	--	%	ISO 4589-2

Injection	Dry	Unit	Test Method
Drying Temperature - Dry Air Dryer	80.0	°C
Drying Time - Dry Air Dryer	2.0 - 6.0	hr
Processing (Melt) Temp	280 - 300	°C
Mold Temperature	80.0 - 120	°C

Note Message
1 .	60x60x2; MT 80°C; 600 Bar
2 .	60x60x2
3 .	60x60x2; MT 80°C; 600 Bar
4 .	60x60x2
5 .	2.0 mm/min
6 .	2.0 mm/min
7 .	2.0 mm/min
8 .	Pull Rate: 2 mm/min; 50% RH
9 .	US-FMVSS302
10 .	-30°C
11 .	23°C
12 .	-30°C
13 .	23°C
14 .	10°C/min
15 .	Procedure A

Resin Grade	Manufacturer	Category	Trademark
NYLAFORCE® B 50	LEIS Polytechnik - polymere Werkstoffe GmbH	Nylon 6	NYLAFORCE®
Hanwha Total PP TB52T	HANWHA TOTAL PETROCHEMICALS Co., Ltd.	PP, Unspecified	Hanwha Total PP
PHOENIX™ 9551	Phon Tech Industrial Company	TPE	PHOENIX™
POCAN® TP 740-101 000000	LANXESS GmbH	PBT+ASA	POCAN®
Delene 2050	Shanghai Lin Gen Rubber Materials Co., Ltd.	TPE	Delene