Chemlon® MDF604 Datasheet,Nylon 6,Teknor Apex Company (Chem Polymer)-SHANGHAI SUSHENG

Message
MDF604 is a 20% glass fibre reinforced, impact modified nylon 6 that offers good rigidity and toughness over a wide temperature range.

General Information
Filler / Reinforcement	Glass fiber reinforced material, 20% filler by weight
Additive	Impact modifier
Features	Impact modification Good toughness Medium hardness
Processing Method	Injection molding

Physical	Nominal Value	Unit	Test Method
Density	1.23	g/cm³	ISO 1183
Molding Shrinkage ¹	0.70 - 1.6	%	Internal method
Water Absorption (Equilibrium, 23°C, 50% RH)	2.1	%	ISO 62

Mechanical	Nominal Value	Unit	Test Method
Tensile Modulus	5500	MPa	ISO 527-2
Tensile Stress	115	MPa	ISO 527-2
Tensile Strain (Break)	8.5	%	ISO 527-2
Flexural Modulus	4500	MPa	ISO 178
Flexural Stress	125	MPa	ISO 178

Impact	Nominal Value	Unit	Test Method
Charpy Notched Impact Strength	20	kJ/m²	ISO 179/1eA
Charpy Unnotched Impact Strength	> 45	kJ/m²	ISO 179/1eU
Notched Izod Impact	16	kJ/m²	ISO 180/A
Unnotched Izod Impact Strength	> 45	kJ/m²	ISO 180

Thermal	Nominal Value	Unit	Test Method
Heat Deflection Temperature
0.45 MPa, not annealed	200	°C	ISO 75-2/B
1.8 MPa, not annealed	190	°C	ISO 75-2/A

Electrical	Nominal Value	Unit	Test Method
Surface Resistivity	1.0E+14	ohms	IEC 60093
Volume Resistivity	1.0E+16	ohms·cm	IEC 60093
Dielectric Strength (3.00 mm)	16	kV/mm	IEC 60243-1

Flammability	Nominal Value	Unit	Test Method
Flame Rating (1.50 mm, Teknor Apex test result)	HB		UL 94

Injection	Nominal Value	Unit
Drying Temperature	80.0	°C
Drying Time	20	hr
Rear Temperature	250 - 280	°C
Middle Temperature	250 - 280	°C
Front Temperature	250 - 280	°C
Processing (Melt) Temp	250 - 290	°C
Mold Temperature	60.0 - 80.0	°C
Injection Rate	Fast
Back Pressure	Moderate
Screw Speed	Moderate

Injection instructions
No drying is necessary unless the material has been exposed to air for longer than three hours. The appearance of splash marks on the surface of mouldings indicates excessive moisture is present.

Note Message
1 .	Mould shrinkage is significantly influenced by many factors including wall thickness, gating, moulding shape and processing conditions. The range values given are determined from specimen bar mouldings of 1.5mm to 4mm wall thickness. They are provided as a guide for comparison purposes only and no guarantee should be inferred from their inclusion. (Specimens measured in the dry state, 24 hours after moulding).

Note Message

1 .

Mould shrinkage is significantly influenced by many factors including wall thickness, gating, moulding shape and processing conditions. The range values given are determined from specimen bar mouldings of 1.5mm to 4mm wall thickness. They are provided as a guide for comparison purposes only and no guarantee should be inferred from their inclusion. (Specimens measured in the dry state, 24 hours after moulding).

Category:	Nylon 6 , Polyamide 6
Manufacturer:	Teknor Apex Company (Chem Polymer)
Trademark:	Chemlon®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	ZRpnm6_Chemlon-MDF604.pdf
PRICE:	Order Products email sales@su-jiao.com

Resin Grade	Manufacturer	Category	Trademark
Shin-Etsu Elastomer SV-57000U	Shin-Etsu Silicones of America	Silicone Rubber, HTV	Shin-Etsu Elastomer
Viton® VTR-8530	DuPont Performance Elastomers	Fluorelastomer	Viton®
ACLAR® 11A (4 mil)	Honeywell	PCTFE	ACLAR®
Aquathene® CM92949	LyondellBasell Industries	Proprietary	Aquathene®
ExxonMobil™ PP7035E4	ExxonMobil Chemical	PP Impact Copolymer	ExxonMobil™