ASTAMID™ MA3WG63
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Marplex Australia Pty. Ltd. |
| Trademark: | ASTAMID™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ZRHiuv_ASTAMID-MA3WG63.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
ASTAMID™ MA3WG63 is a 33% glass reinforced, heat stabilised & UV improved grade of Polyamide 66 (PA 66 or Nylon 66). It is intended for use in metal replacement applications or assemblies requiring high strength, high rigidity, high heat resistance, high chemical resistance and long term durability. This grade is a direct replacement for Maranyl grade A190S. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Specific Gravity | 1.39 | -- | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 0.40 | -- | % | ASTM D955 |
| Water Absorption (24 hr) | 1.6 | -- | % | ASTM D570 |
| Moisture Regain 1 | 5.0 | -- | % | ASTM D570 |
| Hardness | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Rockwell Hardness (M-Scale) | 120 | -- | ASTM D785 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus 2(3.20 mm) | 10000 | 7500 | MPa | ASTM D638 |
| Tensile Strength 3(3.20 mm) | 185 | 135 | MPa | ASTM D638 |
| Tensile Elongation 4(Break, 3.20 mm) | 3.0 | 5.0 | % | ASTM D638 |
| Flexural Modulus 5(3.20 mm) | 9500 | 7250 | MPa | ASTM D790 |
| Flexural Strength 6(3.20 mm) | 280 | 230 | MPa | ASTM D790 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Notched Izod Impact (3.20 mm) | 100 | 150 | J/m | ASTM D256 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 3.20 mm) | 250 | -- | °C | ASTM D648 |
| CLTE - Flow | 1.5E-5 to 2.0E-5 | -- | cm/cm/°C | ASTM D696 |
| Flammability | Dry | Conditioned | Test Method | |
|---|---|---|---|---|
| Flame Rating (1.60 mm) | HB | -- | UL 94 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 75.0 to 85.0 | °C | |
| Drying Time | 2.0 | hr | |
| Rear Temperature | 260 to 280 | °C | |
| Middle Temperature | 270 to 290 | °C | |
| Front Temperature | 280 to 300 | °C | |
| Processing (Melt) Temp | 280 to 310 | °C | |
| Mold Temperature | 50.0 to 80.0 | °C | |
| Injection Pressure | 60.0 to 130 | MPa | |
| Injection Rate | Fast | ||
| Back Pressure | 0.100 to 0.500 | MPa | |
| Screw Speed | 40 to 60 | rpm | |
| Clamp Tonnage | 3.0 to 5.0 | kN/cm² |
| Note Message | |
|---|---|
| 1 . | 65% RH |
| 2 . | 5.0 mm/min |
| 3 . | 5.0 mm/min |
| 4 . | 5.0 mm/min |
| 5 . | 10 mm/min |
| 6 . | 1.3 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| POPELEN GHE-300 | Lotte Chemical Corporation | PP Impact Copolymer | POPELEN |
| SCANLON A 5005B UV | Polykemi AB | ABS+Nylon | SCANLON A |
| TOTAL Polypropylene PPH 3281 | TOTAL Refining & Chemicals | PP Homopolymer | TOTAL Polypropylene |
| Daelim Po1y® DHC-1 | DAELIM INDUSTRIAL CO., LTD. | HDPE | Daelim Po1y® |
| POLYelast TPE ED80 D40 UV | Polykemi AB | PP+EPDM | POLYelast |