An impact-modified and stabilized injection moulding grade for components and housings with good low temperature impact resistance.

General Information
Additive	Impact modifier
Features	Impact modification Low temperature impact resistance Oil resistance
Uses	Shell
Agency Ratings	EC 1907/2006 (REACH)
RoHS Compliance	RoHS compliance
Forms	Particle
Processing Method	Injection molding
Multi-Point Data	Creep Modulus vs. Time (ISO 11403-1) Isochronous Stress vs. Strain (ISO 11403-1) Isothermal Stress vs. Strain (ISO 11403-1) Secant Modulus vs. Strain (ISO 11403-1) Shear Modulus vs. Temperature (ISO 11403-1) Viscosity vs. Shear Rate (ISO 11403-2)

Physical	Dry	Conditioned	Unit	Test Method
Density	1.06	--	g/cm³	ISO 1183
Apparent Density	0.70	--	g/cm³
Melt Volume-Flow Rate (MVR) (275°C/10.0 kg)	38.0	--	cm³/10min	ISO 1133
Water Absorption				ISO 62
Saturated, 23°C	6.7 - 7.7	--	%	ISO 62
Equilibrium, 23°C, 50% RH	2.0 - 2.6	--	%	ISO 62
Mold Shrinkage - constrained ¹	0.85	--	%

Additional Information	Dry	Conditioned		Test Method
Automotive Materials (> 1.00 mm)	Passed	--		FMVSS 302
Polymer Abbreviation	PA66-I	--

Injection	Dry	Unit
Screw Speed		mm/sec

Mechanical	Dry	Conditioned	Unit	Test Method
Tensile Modulus	1900	850	MPa	ISO 527-2
Tensile Stress (Yield)	48.0	40.0	MPa	ISO 527-2/50
Tensile Strain (Yield)	5.0	18	%	ISO 527-2/50
Nominal Tensile Strain at Break	45	> 50	%	ISO 527-2/50
Tensile Creep Modulus ²(1000 hr)	--	450	MPa	ISO 899-1
Flexural Modulus	1750	--	MPa	ISO 178
Flexural Stress	64.0	--	MPa	ISO 178

Impact	Dry	Conditioned	Unit	Test Method
Charpy Notched Impact Strength				ISO 179/1eA
-30°C	31	--	kJ/m²	ISO 179/1eA
23°C	90 kJ/m²	No Break		ISO 179/1eA
Charpy Unnotched Impact Strength (23°C)	No Break	No Break		ISO 179/1eU
Notched Izod Impact				ISO 180/A
-30°C	29	50	kJ/m²	ISO 180/A
23°C	90 kJ/m²	No Break		ISO 180/A

Thermal	Dry	Conditioned	Unit	Test Method
Heat Deflection Temperature
0.45 MPa, not annealed	125	--	°C	ISO 75-2/B
1.8 MPa, not annealed	60.0	--	°C	ISO 75-2/A
Melting Temperature	260	--	°C	ISO 11357-3
CLTE - Flow (23 to 80°C)	7.0E-5 - 1.0E-4	--	cm/cm/°C	ISO 11359-2
Specific Heat	1700	--	J/kg/°C
Thermal Conductivity	0.33	--	W/m/K	DIN 52612

Electrical	Dry	Conditioned	Unit	Test Method
Surface Resistivity	--	1.0E+12	ohms	IEC 60093
Volume Resistivity	4.0E+14	1.0E+12	ohms·cm	IEC 60093
Relative Permittivity (1 MHz)	3.10	3.60		IEC 60250
Dissipation Factor (1 MHz)	0.016	0.070		IEC 60250
Comparative Tracking Index (Solution A)	600	--	V	IEC 60112

Flammability	Dry	Conditioned	Unit	Test Method
Flame Rating (1.60 mm)	HB	--		UL 94

Injection	Dry	Unit
Drying Temperature	80.0	°C
Drying Time	4.0	hr
Suggested Max Moisture	0.15	%
Hopper Temperature	80.0	°C
Rear Temperature	290	°C
Middle Temperature	290	°C
Front Temperature	290	°C
Nozzle Temperature	290	°C
Processing (Melt) Temp	280 - 300	°C
Mold Temperature	60.0 - 80.0	°C

Injection instructions
Residence Time : <10 min

Note Message
1 .	Test box with central gating, dimensions of base (107471,5) mm, processing condition: TM = 290°C, TW = 60°C
2 .	strain <= 0.5%, 23°C

Resin Grade	Manufacturer	Category	Trademark
RTP 205.3 HS GE	RTP Company	Nylon 66	RTP
Tecopet® PT74 GR20 BK002 XA20	Eurotec Engineering Plastics	PET	Tecopet®
Bergamid™ A700 G15 H W UF GN046	PolyOne Corporation	Nylon 66	Bergamid™
Grivory® XE 4065 black 9238	EMS-GRIVORY	Nylon 10T/X	Grivory®
Karina BLACK PVC COMPOUND 852-48/ 1-F-IS-BZ	Karina Ind. e Com. de Plásticos Ltda	PVC, Unspecified	Karina