Akulon® S223-HG7
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | DSM Engineering Plastics |
| Trademark: | Akulon® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ZQHunY_Akulon-S223-HG7.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Akulon® S223-HG7 is a Polyamide 66 (Nylon 66) material filled with 35% glass fiber. It is available in Asia Pacific, Europe, or North America. Important attributes of Akulon® S223-HG7 are:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Forms |
|
| Multi-Point Data |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.41 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | |||
| Across Flow | 1.4 | -- | % | |
| Flow | 0.54 | -- | % | |
| Water Absorption | ISO 62 | |||
| Saturation, 23°C | 5.5 | -- | % | |
| Equilibrium, 23°C, 50% RH | 1.5 | -- | % |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 11000 | 7500 | MPa | ISO 527-2 |
| Tensile Stress (Break) | 200 | 130 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 3.0 | 6.0 | % | ISO 527-2 |
| Flexural Modulus | 9400 | -- | MPa | ISO 178 |
| Flexural Stress | 270 | -- | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -30°C | 11 | 11 | kJ/m² | |
| 23°C | 13 | 21 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -30°C | 75 | 75 | kJ/m² | |
| 23°C | 95 | 110 | kJ/m² |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, Unannealed | 260 | -- | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 250 | -- | °C | ISO 75-2/A |
| Melting Temperature 1 | 260 | -- | °C | ISO 11357-3 |
| CLTE | ISO 11359-2 | |||
| Flow | 2.0E-5 | -- | cm/cm/°C | |
| Transverse | 6.0E-5 | -- | cm/cm/°C |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | -- | 1.0E+13 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+14 | 1.0E+12 | ohms·cm | IEC 60093 |
| Electric Strength | 35 | 30 | kV/mm | IEC 60243-1 |
| Relative Permittivity | IEC 60250 | |||
| 100 Hz | 4.00 | 10.0 | ||
| 1 MHz | 3.60 | 4.00 | ||
| Dissipation Factor | IEC 60250 | |||
| 100 Hz | 5.0E-3 | 0.30 | ||
| 1 MHz | 0.014 | 0.10 | ||
| Comparative Tracking Index | 500 | 500 | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flammability Classification | IEC 60695-11-10, -20 | |||
| 0.710 mm | HB | -- | ||
| 1.50 mm | HB | -- |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 4.0 to 8.0 | hr | |
| Rear Temperature | 275 to 295 | °C | |
| Middle Temperature | 275 to 295 | °C | |
| Front Temperature | 275 to 290 | °C | |
| Nozzle Temperature | 280 to 290 | °C | |
| Processing (Melt) Temp | 280 to 305 | °C | |
| Mold Temperature | 50.0 to 80.0 | °C | |
| Injection Rate | Moderate-Fast | ||
| Back Pressure | 3.00 to 10.0 | MPa | |
| Screw Compression Ratio | 2.5:1.0 |
| Note Message | |
|---|---|
| 1 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 2581 HEC FR | RTP Company | PC+ABS | RTP |
| S-RIM™ 6260 Black | Hapco Inc. | TP, Unspecified | S-RIM™ |
| TECAFINE® HDPE | Ensinger Inc. | HDPE | TECAFINE® |
| Witcom PA66 6G/3L1 | Witcom Engineering Plastics B.V. | Nylon 66 | Witcom PA66 |
| EcoPaXX® Q-E7300 | DSM Engineering Plastics | Nylon 410 | EcoPaXX® |