TOTAL Polystyrene Impact 6540
| Category: | PS (HIPS) , High Impact Polystyrene |
| Manufacturer: | TOTAL Refining & Chemicals |
| Trademark: | TOTAL Polystyrene |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ZPHGU9_TOTAL-Polystyrene-Impact-6540.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
POLYSTYRENE IMPACT 6541 is an easy flowing, high impact polystyrene with a good balance of mechanical and thermal properties. This resin combines physical properties such as the flow necessary for large or complex mouldings, the impact resistance for good mechanical properties in thin wall sections and good thermal properties for articles subjected to elevated temperatures in use. The combination of properties also offers high productivity. POLYSTYRENE IMPACT 6540 satifies the requirements of a wide range of molding applications. Toys, television housings, food packaging, refrigerator, computer keyboards, office equipment, household items... |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.04 | g/cm³ | ISO 1183 |
| Apparent Density | 0.60 | g/cm³ | |
| Melt Mass-Flow Rate (MFR) (200°C/5.0 kg) | 12 | g/10 min | ISO 1133 |
| Molding Shrinkage | 0.40 to 0.70 | % | |
| Water Absorption (23°C, 24 hr) | < 0.10 | % | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 78 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ISO 527-2 | ||
| Yield, 23°C, Injection Molded | 25.0 | MPa | |
| Break, 23°C, Injection Molded | 20.0 | MPa | |
| Tensile Strain (Break, 23°C, Injection Molded) | 45 | % | ISO 527-2 |
| Flexural Modulus (23°C, Injection Molded) | 2100 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength (23°C, Injection Molded) | 9.5 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | ISO 75-2/A | ||
| 1.8 MPa, Unannealed | 68.0 | °C | |
| 1.8 MPa, Annealed | 80.0 | °C | |
| Vicat Softening Temperature | |||
| -- | 92.0 | °C | ISO 306/A50 |
| -- | 83.0 | °C | ISO 306/B50 |
| CLTE - Flow | 9.1E-5 | cm/cm/°C | ISO 11359-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | > 1.0E+13 | ohms | IEC 60093 |
| Electric Strength | 150 | kV/mm | IEC 60243-1 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TECHNYL STAR™ SX 218L2 V60 BLACK JA6A | Solvay Engineering Plastics | Nylon 6 | TECHNYL STAR™ |
| Sylvin 8426-70 Black | Sylvin Technologies Incorporated | PVC+PUR | Sylvin |
| ICORENE® 4014 | ICO Polymers EMEA, A Division of A. Schulman | PP Copolymer | ICORENE® |
| PHOENIX™ 1203 | Phon Tech Industrial Company | SBC | PHOENIX™ |
| Hostacom X M3 T14 C11295 | LyondellBasell Industries | PP Copolymer | Hostacom |