XYRON™ EV103
| Category: | PPE+PP , Polyphenylene Ether + PP |
| Manufacturer: | Asahi Kasei Chemicals Corporation |
| Trademark: | XYRON™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ZO6qv3_XYRON-EV103.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Modified PPE PP/PPE alloy Non-reinforced Dimensional stability Good |
| General Information | |
|---|---|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.928 | g/cm³ | ISO 1183 |
| Molding Shrinkage 1(3.00 mm) | 2.0 to 2.5 | % | Internal Method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Yield, 23°C) | 37.0 | MPa | ISO 527-2 |
| Tensile Strain (Break, 23°C) | 51 | % | ISO 527-2 |
| Flexural Modulus (23°C) | 2050 | MPa | ISO 178 |
| Flexural Stress (23°C) | 57.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 2(23°C) | 19 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, Unannealed | 97.0 | °C | ASTM D648 |
| 1.8 MPa, Unannealed | 90.0 | °C | ISO 75-2/A |
| CLTE - Flow (-30 to 65°C) | 9.0E-5 | cm/cm/°C | ISO 11359-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity (23°C) | 8.4E+16 | ohms·cm | IEC 60093 |
| Electric Strength 3(2.00 mm) | 30 | kV/mm | IEC 60243-1 |
| Dielectric Constant | IEC 60250 | ||
| 100 Hz | 2.30 | ||
| 1 MHz | 2.30 | ||
| Dissipation Factor | IEC 60250 | ||
| 100 Hz | 2.0E-4 | ||
| 1 MHz | 5.0E-4 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 to 90.0 | °C | |
| Drying Time | 1.0 to 2.0 | hr | |
| Processing (Melt) Temp | 230 to 260 | °C | |
| Mold Temperature | 50.0 to 70.0 | °C |
| Note Message | |
|---|---|
| 1 . | 120x80x3 mm |
| 2 . | 4 mm |
| 3 . | Short Time |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Mar-Bal MB1000-15 | Mar-Bal, Inc. | Polyester, TP | Mar-Bal |
| Advanced Composites ADX-5001 | Advanced Composites, Inc. | PP, Unspecified | Advanced Composites |
| Celanex® 2004-2 | Celanese Corporation | PBT | Celanex® |
| Lucent PP GPP-320 | Lucent Polymers, Inc. | PP, Unspecified | Lucent PP |
| POCAN® ECO T 3230 000000 | LANXESS Corporation | PBT+PET | POCAN® |