Braskem PE PLURIS6301
| Category: | LLDPE , Linear Low Density Polyethylene |
| Manufacturer: | Braskem |
| Trademark: | Braskem PE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ZMu93H_Braskem-PE-PLURIS6301.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Pluris6301 is a Braskem Quatropolymer produced with Spherilene technology. This grade show unique properties, such as high stiffness associated with toughness. In addition to good processability, also shows a very good bubble stability and very low gel content. Applications: Frozen bags, high performance structures (coextrusion) for automatic packaging (FFS). Additive:
Process: Blown Film Extrusion |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.919 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 0.85 | g/10 min | ASTM D1238 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | ASTM D882 | ||
| MD : Fracture, 38 µm | 40.0 | MPa | ASTM D882 |
| TD : Fracture, 38 µm | 30.0 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : Fracture, 38 µm | 900 | % | ASTM D882 |
| TD : Fracture, 38 µm | 1200 | % | ASTM D882 |
| Flexural Modulus | ASTM D790 | ||
| 1% Secant, MD : 38 µm | 250 | MPa | ASTM D790 |
| 1% Secant, TD : 38 µm | 300 | MPa | ASTM D790 |
| Dart Drop Impact 1(38 µm) | 140 | g | ASTM D1709 |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 38 µm | 80 | g | ASTM D1922 |
| TD : 38 µm | 610 | g | ASTM D1922 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (60°, 38.0 µm) | 102 | ASTM D2457 | |
| Haze | 11 | % | ASTM D1003 |
| Extrusion instructions |
|---|
| Recommended Blown Film Extrusion Conditions: Temperature Profile: 190°C to 220°C Blow Up Ratio: 2 to 3.5:1 Die Gap: 1.8 to 2.5 mm Screen Package: 40/60/40 mesh Mass Temperature: >220°C |
| Note Message | |
|---|---|
| 1 . | F50 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| tivilon® M 52 DX 4 | API SpA | TPV | tivilon® |
| TOTAL Polyethylene CD-471 | TOTAL Refining & Chemicals | HDPE | TOTAL Polyethylene |
| Celstran® PP-GF30-0405 P10 | Celanese Corporation | PP, Unspecified | Celstran® |
| Karina BLACK PVC COMPOUND 956-48/1-C-IS (*) | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Hostacom EKC 330N G72366 | LyondellBasell Industries | PP Copolymer | Hostacom |