Vipel® F010-INL-00
| Category: | Vinyl Ester , Vinyl Ester |
| Manufacturer: | AOC, L.L.C. |
| Trademark: | Vipel® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ZMHt2z_VipelF010INL00.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
AOC's Vipel F010 series is a bisphenol A epoxy-based vinyl ester resin dissolved in styrene. The Vipel F010 series is ideally suited for use in hand lay-up, spray-up, filament winding, SMC, and pultrusion processes where outstanding mechanical properties and excellent resistance to chemicals and heat are required. BENEFITS Versatile Wide formulating capabilities allow for use in many processes and for optimization of cost/performance. Unique composition produces a tough and versatile resin with excellent crack and craze resistance in molded parts. Vipel F010 is suitable for moldings that are subjected to particularly high static or dynamic loads, such as pipe, tanks, duct work and flooring applications. Vinyl ester resins have excellent resistance to sustained heat. Corrosion Resistance Vipel F010 is highly resistant to hydrogen peroxide, and alkalis, and performs well in various stages of hypochlorite and chlorine production. Refer to AOC's "Corrosion Resistant Resin Guide" for corrosion resistance information or for questions regarding suitability of a resin to any particular chemical environment contact AOC. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Styrene Content | 43 | % |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Critical Strain Energy | 100 | J/m² | ASTM E399 |
| Gel to Peak | 1.0 | hr | |
| Peak Exotherm | 80 | °C | |
| Stress Intensity Factor | 0.600 | ASTM E399 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Barcol Hardness | 39 | ASTM D2583 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 3170 | MPa | ASTM D638 |
| Tensile Strength | 88.3 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 6.2 | % | ASTM D638 |
| Flexural Modulus | 3450 | MPa | ASTM D790 |
| Flexural Strength | 152 | MPa | ASTM D790 |
| Compressive Strength | 121 | MPa | ASTM D695 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 120 | °C | ASTM D648 |
| Glass Transition Temperature | 130 | °C | DIN 53445 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | > 1.0E+13 | ohms | DIN 53482 |
| Volume Resistivity 1 | > 1.0E+16 | ohms·cm | DIN 53482 |
| Dielectric Strength (0.700 mm) | 120 | kV/mm | DIN 53481 |
| Dielectric Constant | DIN 53483 | ||
| 60 Hz 2 | 3.40 | DIN 53483 | |
| 60 Hz 3 | 3.50 | DIN 53483 | |
| 1 kHz 4 | 3.40 | DIN 53483 | |
| 1 kHz 5 | 3.50 | DIN 53483 | |
| 1 MHz 6 | 3.30 | DIN 53483 | |
| 1 MHz 7 | 3.40 | DIN 53483 | |
| Dissipation Factor | DIN 53483 | ||
| 60 Hz 8 | 2.5E-3 | DIN 53483 | |
| 60 Hz 9 | 3.7E-3 | DIN 53483 | |
| 1 kHz 10 | 2.2E-3 | DIN 53483 | |
| 1 kHz 11 | 3.3E-3 | DIN 53483 | |
| 1 MHz 12 | 1.6E-3 | DIN 53483 | |
| 1 MHz 13 | 2.3E-3 | DIN 53483 |
| Uncured Properties | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.01 | g/cm³ | |
| Viscosity (25°C, Brookfield LV) | 0.13 | Pa·s | |
| Gel Time (25°C) | 47 | min |
| Note Message | |
|---|---|
| 1 . | Dry |
| 2 . | Dry |
| 3 . | after 24 hrs in drinking water |
| 4 . | Dry |
| 5 . | after 24 hrs in drinking water |
| 6 . | Dry |
| 7 . | after 24 hrs in drinking water |
| 8 . | Dry |
| 9 . | after 24 hrs in drinking water |
| 10 . | Dry |
| 11 . | after 24 hrs in drinking water |
| 12 . | Dry |
| 13 . | after 24 hrs in drinking water |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TRISTAR® PC-10FR-(16) | Polymer Technology and Services, LLC | PC | TRISTAR® |
| VAMPAMID 66 3026 V0 | Vamp Tech | Nylon 66 | VAMPAMID |
| NEFTEKHIM PP 1553L | Nizhnekamskneftekhim Inc. | PP Homopolymer | NEFTEKHIM PP |
| AKROMID® A3 GF 35 S1 black (2717) | AKRO-PLASTIC GmbH | Nylon 66 | AKROMID® |
| Laprene® 830000545 | SO.F.TER. SPA | SEBS | Laprene® |