Order Products : sales@su-jiao.com
DynaStat® 2247-X
| Category: | Nylon 12 , Polyamide 12 |
| Manufacturer: | Polymer Dynamix |
| Trademark: | DynaStat® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ZL0P7k_DynaStat-2247-X.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Antistatic Polyamide 12 Compound Features:
Applications:
|
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Processing Method |
|
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 434 | MPa | ASTM D638 |
| Tensile Strength | ASTM D638 | ||
| Yield | 26.2 | MPa | ASTM D638 |
| Fracture | 31.7 | MPa | ASTM D638 |
| Tensile Elongation | ASTM D638 | ||
| Yield | 30 | % | ASTM D638 |
| Fracture | > 200 | % | ASTM D638 |
| Flexural Modulus | 552 | MPa | ASTM D790 |
| Flexural Strength | 23.8 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.18 mm) | No Break | ASTM D256 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+6 - 1.0E+8 | ohms | ASTM D257 |
| Static Decay | sec | NFPA 99 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 71.1 - 82.2 | °C | |
| Drying Time | 3.0 - 5.0 | hr | |
| Rear Temperature | 193 - 204 | °C | |
| Middle Temperature | 199 - 210 | °C | |
| Front Temperature | 204 - 216 | °C | |
| Nozzle Temperature | 210 - 221 | °C | |
| Processing (Melt) Temp | 210 - 221 | °C | |
| Mold Temperature | 10.0 - 65.6 | °C | |
| Injection Pressure | 68.9 - 138 | MPa | |
| Injection Rate | Moderate | ||
| Back Pressure | 0.345 - 0.689 | MPa | |
| Screw Speed | 40 - 70 | rpm | |
| Clamp Tonnage | 5.5 - 8.3 | kN/cm² |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 71.1 - 82.2 | °C | |
| Drying Time | 3.0 - 5.0 | hr | |
| Cylinder Zone 1 Temp. | 193 - 204 | °C | |
| Cylinder Zone 3 Temp. | 199 - 210 | °C | |
| Cylinder Zone 5 Temp. | 204 - 216 | °C | |
| Melt Temperature | 210 - 221 | °C | |
| Die Temperature | 210 - 221 | °C |
| Extrusion instructions |
|---|
| Screw Speed: 25 to 100 RPM |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sup-tech T601 | Shanghai Suptech Engineering Plastics Co. Ltd. | PBT | Sup-tech |
| VITAMIDE® BR17 | A. Schulman Europe | Nylon 6 | VITAMIDE® |
| Unichem 4260-85 | Colorite Polymers | PVC, Flexible | Unichem |
| Novomer NB-20 | Novomer, Inc. | PC | Novomer |
| Karina GRAY COLOR CONCENTRATE 18/355-FC | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |