Pro-fax SA861
| Category: | PP Random Copolymer , Polypropylene Random Copolymer |
| Manufacturer: | LyondellBasell Industries |
| Trademark: | Pro-fax |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ZKzYDH_Pro-fax-SA861.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Pro-fax SA-861 polypropylene random copolymer resin, formulated with slip and antiblock, is designed for cast film packaging applications. Cast film made with this resin has exceptional clarity and gloss, as well as improved cold temperature impact resistance and broader heat seal range compared to homopolymer polypropylene. Typical applications include bags for hosiery, shirts and other textiles, produce packaging, sheet protectors, photograph pockets and card display sleeves. For regulatory compliance information see Pro-fax SA861 Regulatory Affairs Product Stewardship Information/Certification Data Sheet (RAPIDS). |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.900 | g/cm³ | ASTM D792B |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 6.5 | g/10 min | ASTM D1238 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield) | 27.6 | MPa | ASTM D638 |
| Tensile Elongation (Yield) | 13 | % | ASTM D638 |
| Flexural Modulus - 1% Secant 1 | 896 | MPa | ASTM D790A |
| Coefficient of Friction | 0.15 to 0.25 | ASTM D1894 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 25 | µm | |
| Secant Modulus | ASTM D882 | ||
| 1% Secant, MD : 25 µm | 655 | MPa | |
| 1% Secant, TD : 25 µm | 621 | MPa | |
| Tensile Strength | ASTM D882 | ||
| MD : Yield, 25 µm | 49.0 | MPa | |
| TD : Yield, 25 µm | 32.4 | MPa | |
| Tensile Elongation | ASTM D882 | ||
| MD : Break, 25 µm | 730 | % | |
| TD : Break, 25 µm | 710 | % | |
| Dart Drop Impact | ASTM D1709 | ||
| 0°C, 25 µm | 360 | g | |
| 23°C, 25 µm | 1900 | g | |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 25 µm | 25 | g | |
| TD : 25 µm | 500 | g | |
| Seal Initiation Temperature (25 µm) | 135 | °C | |
| Dart Drop Test | ASTM D1709 | ||
| 0°C, 25.0 µm | 35.6 | J/cm | |
| 23°C, 25.0 µm | 187 | J/cm |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 69 | J/m | ASTM D256A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed) | 76.1 | °C | ASTM D648 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°, 25.0 µm) | 80 to 85 | ASTM D2457 | |
| Haze (25.0 µm) | 3.0 | % | ASTM D1003 |
| Note Message | |
|---|---|
| 1 . | 1.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| PONACOM PE 8420 | Ponachem Compound GmbH | HDPE | PONACOM PE |
| RTP 2800 B-75A HF | RTP Company | TPV | RTP |
| Quadrant EPP PVC, Type I, Grade 1 | Quadrant Engineering Plastic Products | PVC, Unspecified | Quadrant EPP |
| Sup-tech A706SH | Shanghai Suptech Engineering Plastics Co. Ltd. | Nylon, Unspecified | Sup-tech |
| OTECH ALLOY OTE8840 - Calendering | OTECH Corporation | TP, Unspecified | OTECH ALLOY |