Ultraform® Z 2320 0035
| Category: | Acetal (POM) Copolymer , Acetal (POM) Copolymer |
| Manufacturer: | BASF Corporation |
| Trademark: | Ultraform® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ZINmW8_Ultraform-Z-2320-0035.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Extremely easy flowing grade for very thin-walled moldings with difficult flow path to wall thickness ratios and very short cycle times. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Forms |
|
| Processing Method |
|
| Resin ID (ISO 1043) |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.40 | g/cm³ | ISO 1183 |
| Apparent Density | 0.85 | g/cm³ | |
| Melt Volume-Flow Rate (MVR) (190°C/2.16 kg) | 85.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage | ISO 294-4 | ||
| Vertical flow direction | 2.1 | % | ISO 294-4 |
| Flow direction | 2.0 | % | ISO 294-4 |
| Water Absorption | ISO 62 | ||
| Saturated, 23°C | 0.80 | % | ISO 62 |
| Equilibrium, 23°C, 50% RH | 0.20 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2600 | MPa | ISO 527-2 |
| Tensile Stress (Yield) | 63.0 | MPa | ISO 527-2/50 |
| Tensile Strain (Yield) | 8.0 | % | ISO 527-2/50 |
| Nominal Tensile Strain at Break | 13 | % | ISO 527-2/50 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 3.5 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 140 | kJ/m² | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melting Temperature | 167 | °C | ISO 11357-3 |
| CLTE - Flow (23 to 55°C) | 1.1E-4 | cm/cm/°C | ISO 11359-2 |
| Maximum operating temperature- short cycle operation | 100 | °C |
| Additional Information | Nominal Value | Test Method | |
|---|---|---|---|
| ISO Type | POM-K, M-GNR, 06-002 | ISO 9988-1 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Screw Speed | mm/sec |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+13 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+15 | ohms·cm | IEC 60093 |
| Relative Permittivity (1 MHz) | 3.80 | IEC 60250 | |
| Dissipation Factor (1 MHz) | 5.0E-3 | IEC 60250 | |
| Comparative Tracking Index (Solution A) | 600 | V | IEC 60112 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 100 | °C | |
| Drying Time | 3.0 | hr | |
| Suggested Max Moisture | 0.20 | % | |
| Hopper Temperature | 200 | °C | |
| Rear Temperature | 200 | °C | |
| Middle Temperature | 200 | °C | |
| Front Temperature | 200 | °C | |
| Nozzle Temperature | 200 | °C | |
| Processing (Melt) Temp | 190 - 230 | °C | |
| Mold Temperature | 60.0 - 120 | °C |
| Injection instructions |
|---|
| Residence Time : <10 min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SureSpec LD20-004 | Genesis Polymers | LDPE | SureSpec |
| TOTAL Polyethylene HDPE 9458 | TOTAL Refining & Chemicals | HDPE, MMW | TOTAL Polyethylene |
| Unichem 7816 | Colorite Polymers | PVC, Unspecified | Unichem |
| NEMCON E PC CB | Ovation Polymers Inc. | PC | NEMCON E |
| CoREZYN® COR45-BA-637 | Interplastic Corporation | Vinyl Ester | CoREZYN® |