Elastomer modified polypropylene copolymer, 10% mineral filled |
General Information | |
---|---|
Filler / Reinforcement |
|
Features |
|
Uses |
|
Agency Ratings |
|
Appearance |
|
Processing Method |
|
Physical | Nominal Value | Unit | Test Method |
---|---|---|---|
Specific Gravity | 0.970 | g/cm³ | ASTM D792 |
Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 16 | g/10 min | ASTM D1238 |
Molding Shrinkage | 1.1 | % | Internal Method |
Mechanical | Nominal Value | Unit | Test Method |
---|---|---|---|
Tensile Strength (Yield) | 18.0 | MPa | ASTM D638 |
Tensile Elongation (Break) | 100 | % | ASTM D638 |
Flexural Modulus | 1300 | MPa | ASTM D790 |
Impact | Nominal Value | Unit | Test Method |
---|---|---|---|
Notched Izod Impact (23°C) | 390 | J/m | ASTM D256 |
Thermal | Nominal Value | Unit | Test Method |
---|---|---|---|
Deflection Temperature Under Load (1.8 MPa, Unannealed) | 52.0 | °C | ASTM D648 |
Vicat Softening Temperature | 51.0 | °C | ASTM D1525 1 |
Flammability | Nominal Value | Test Method | |
---|---|---|---|
Flame Rating | UL 94 | ||
1.60 mm | HB | ||
3.20 mm | HB |
Injection | Nominal Value | Unit | |
---|---|---|---|
Rear Temperature | 190 | °C | |
Middle Temperature | 210 | °C | |
Front Temperature | 230 | °C | |
Mold Temperature | 40.0 to 60.0 | °C |
Note Message | |
---|---|
1 . | Rate A (50°C/h), Loading 1 (10 N) |
Resin Grade | Manufacturer | Category | Trademark |
---|---|---|---|
MAXAMID™ PA66G33UTL-NC010 | Pier One Polymers, Inc. | Nylon 66 | MAXAMID™ |
STRANOX H-PP40%LFT | Oxford Polymers | PP Homopolymer | STRANOX |
Bio-Flex® S 9533 | FKuR Kunststoff GmbH | Biodeg Polymers | Bio-Flex® |
Hostacom EKC 318D NAT | LyondellBasell Industries | PP Copolymer | Hostacom |
PENTAMID B GK15 H natural | PENTAC Polymer GmbH | Nylon 6 | PENTAMID B |