Bayflex® XGT-2 (50% BaSO4)
| Category: | PUR-MDI , Polyurethane (MDI) |
| Manufacturer: | Covestro - PUR |
| Trademark: | Bayflex® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ZGvxX6_Bayflex-XGT-2-50-BaSO4-.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Bayflex XGT 2 is an elastomeric polyurethane system used in the reaction injection molding (RIM) process. The system is supplied as two liquid components: Component A is a modified diphenylmethane diisocyanate (MDI), and Component B is a polyether polyol system. The extended gel time of Bayflex XGT 2 gives equipment designers the flexibility to create large, complex parts that can be molded on existing injection machinery. The resin's soft feel and the ability to tailor part density through the addition of barium sulfate make this product ideal for applications that require some level of sound absorption, such as floor coverings in heavy trucks or equipment. In addition, the material is soft enough to be used for producing seals, gaskets and wire harness type applications. As with any product, use of the Bayflex XGT 2 system in a given application must be tested (including field testing, etc.) in advance by the user to determine suitability. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.66 | g/cm³ | ASTM D1622, ASTM D1505 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness | ASTM D2240 | ||
| Shaw A, 1 sec | 80 | ASTM D2240 | |
| Shaw A, 5 seconds | 78 | ASTM D2240 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | ASTM D412 | ||
| Transverse flow : Yield 1 | 5.00 | MPa | ASTM D412 |
| Transverse flow : Yield 2 | 5.82 | MPa | ASTM D412 |
| Flow : Yield 3 | 5.10 | MPa | ASTM D412 |
| Flow : Yield 4 | 5.87 | MPa | ASTM D412 |
| Tensile Elongation | ASTM D412 | ||
| Transverse flow : Fracture 5 | 250 | % | ASTM D412 |
| Flow : Fracture 6 | 250 | % | ASTM D412 |
| Transverse flow : Fracture 7 | 280 | % | ASTM D412 |
| Flow : Fracture 8 | 270 | % | ASTM D412 |
| Tear Strength | |||
| Transverse flow 9 | 5.27 | kN/m | ASTM D1938 |
| Flow 10 | 4.24 | kN/m | ASTM D1938 |
| Transverse flow 11 | 17.1 | kN/m | ASTM D624 |
| Flow 12 | 16.5 | kN/m | ASTM D624 |
| Compression Set | 27 | % | ASTM D395B |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flammability | Pass | FMVSS 302 |
| Additional Information | Nominal Value | Test Method | |
|---|---|---|---|
| Low temperature toughness- 16 hr (-29°C) | Pass | SAE J80 |
| Thermoset | Nominal Value | Test Method | |
|---|---|---|---|
| Thermoset Components | |||
| Component a | Mixing ratio by weight: 16 | ||
| Component B | Mixing ratio by weight: 100 |
| Additional Information | Nominal Value | Test Method | |
|---|---|---|---|
| Part A Type: Isocyanate Specific Gravity @ 25°C: 1.21 Viscosity @25°C: 700 mPa-s Flash Point PMCC: 213 °C NCO: 22.6 to 23.1 wt% Part B Type: Polyol Specific Gravity @ 25°C: 1.86 Viscosity @25°C: 8000 mPa-s Flash Point PMCC: 114 °C Water: 0.09 wt% max Molding Parameters Isocyanate Temperature: 38 to 43°C Slurry Temperature: 63 to 68°C Slurry or Polyol Nucleation: 5 to 10% Maximum Shot Time: 7 sec Typical Cure Time, 0.125 in: 3 min Slurry Mixing Ratio, Polyol/BaSO4, by weight: 100/138 Polyol Mixhead Pressure: 1700 to 1800 psi Isocyanate Mixhead Pressure: 1850 to 1950 psi |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Mold Temperature | 65.6 - 76.7 | °C |
| Note Message | |
|---|---|
| 1 . | 510 mm/min |
| 2 . | C mold, 510 mm/min, aging 70 hr at 70°C |
| 3 . | C mold, 510mm/min |
| 4 . | C mold, 510 mm/min, aging 70 hr at 70°C |
| 5 . | 510 mm/min |
| 6 . | 510 mm/min |
| 7 . | Mouth Model C, 510 mm/min, aging 70 hr at 70°C |
| 8 . | Mouth Model C, 510 mm/min, aging 70 hr at 70°C |
| 9 . | Split |
| 10 . | Split |
| 11 . | C mould |
| 12 . | C mould |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sinvicomp SIM4107 | Teknor Apex Asia Pacific PTE. LTD. | PVC, Flexible | Sinvicomp |
| Bergamid™ A70 G30 U NC284 | PolyOne Corporation | Nylon 66 | Bergamid™ |
| MAJORIS DW444X/8 | AD majoris | PP, Unspecified | MAJORIS |
| ExxonMobil™ PP6272NE1 | ExxonMobil Chemical | PP Homopolymer | ExxonMobil™ |
| ALCOM® LB PC 1000 14073 WT1164-14 | ALBIS PLASTIC GmbH | PC | ALCOM® LB |