Makroblend庐 UT250
| Category: | PC+PET , Polycarbonate + PET |
| Manufacturer: | Covestro - Polycarbonates |
| Trademark: | Makroblend® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ZE7FaQ_Makroblend-UT250.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| (PC+PET)-blend, impact modified, easy release, injection molding. Makroblend UT250 offers high heat resistance, good chemical resistance and flowability. Additionally, molded parts from UT250 having exceptional dimensional stability. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melt Volume-Flow Rate (MVR) (265°C/5.0 kg) | 22.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage | ISO 2577 | ||
| Across Flow 1 | 0.60 to 0.80 | % | |
| Across Flow : 90°C, 1 hr | 0.10 to 0.20 | % | |
| Flow 2 | 0.60 to 0.80 | % | |
| Flow : 90°C, 1 hr | 0.10 to 0.20 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 2250 | MPa | ISO 527-2/1 |
| Tensile Stress | ISO 527-2/50 | ||
| Yield, 23°C | 55.0 | MPa | |
| Break, 23°C | 50.0 | MPa | |
| Tensile Strain (Yield, 23°C) | 5.0 | % | ISO 527-2/50 |
| Nominal Tensile Strain at Break (23°C) | > 50 | % | ISO 527-2/50 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength | |||
| -30°C | No Break | ISO 180/1C | |
| -20°C | 40 | kJ/m² | ISO 180/A |
| 23°C | 50 | kJ/m² | ISO 180/A |
| 23°C | No Break | ISO 180/1C |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 125 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 110 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 140 | °C | ISO 306/B120 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 110 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | < 0.010 | % |
| Note Message | |
|---|---|
| 1 . | 600 bar |
| 2 . | 600 bar |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Siloxane Masterbatch MB50-320 | Multibase, A Dow Corning Company | Siloxane, UHMW | Siloxane Masterbatch |
| INEOS HDPE HP50-25-153 | INEOS Olefins & Polymers USA | HDPE Copolymer | INEOS HDPE |
| Karina CLEAR PVC COMPOUND 95/222-D-AT-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Karina CLEAR PVC COMPOUND 80/218-IS-RG | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| SIBUR Synthetic Rubber SSBR-2560 TDAE Grade C | SIBUR | SBR, Solution | SIBUR Synthetic Rubber |