BESTNYL SC00VI02AH15
| Category: | Nylon 66/6 , Polyamide 66/6 Copolymer |
| Manufacturer: | Triesa Plastics |
| Trademark: | BESTNYL |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ZDhsav_BESTNYL-SC00VI02AH15.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Polyamide 6 polyamide 6.6 (PA 6/6.6) black and heat stabilized with 30% mineral charge, is characterized for its great dimensional stability, good superficial finish, good in machine and release mould behaviour. Currently used in injection pieces that are not required to endure mechanical efforts,but with a great deal of importance in final appearance and dimensionality. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.36 | g/cm³ | ISO 1183 |
| Molding Shrinkage | 0.80 | % | ISO 294-4 |
| Water Absorption (23°C, 24 hr) | 2.0 | % | ISO 62 |
| Ash Content | 30 | % | Internal Method |
| Humidity - Pellets | 0.20 | % | ISO 1110 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore D) | 81 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 5800 | MPa | ISO 527-2 |
| Tensile Stress | 80.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 3.0 | % | ISO 527-2 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 5.0 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength (23°C) | 45 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (0.45 MPa, Unannealed) | 110 | °C | ISO 75-2/B |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+11 | ohms | IEC 60093 |
| Electric Strength | 28 | kV/mm | IEC 60243-1 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Burning Rate | < 100 | mm/min | FMVSS 302 |
| Flame Rating | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 100 | °C | |
| Drying Time | 3.0 to 4.0 | hr | |
| Processing (Melt) Temp | 270 to 280 | °C | |
| Mold Temperature | 80.0 to 90.0 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| ProvaMed® TPE 1060 | ACTEGA GmbH | TPE | ProvaMed® TPE |
| Trilene® HI35HO | Chandra Asri Petrochemical | PP Homopolymer | Trilene® |
| ALCOM® PC 740/1.1 CF10 | ALBIS PLASTIC GmbH | PC | ALCOM® PC |
| Flontech® FT-STST50-6 | Guarniflon S.p.A. - Flontech Division | PTFE | Flontech® |
| Lucent TPO TPO-30T | Lucent Polymers, Inc. | Polyolefin, Unspecified | Lucent TPO |