Ebalta GM 979 / PUR 1
| Category: | PUR, Unspecified , Polyurethane |
| Manufacturer: | Ebalta Kunststoff GmbH |
| Trademark: | Ebalta |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Z8wk5b_Ebalta-GM-979-PUR-1.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
ebalta GM 979 is an easy-to-handle-2components-polyurethane casting compound which shows very low adhesive properties compared to moulding sand. Due to its high abrasion resistance, GM 979 is especially suitable for foundry patterns, which have to resist to abrasive wear by moulded sand. GM 979 even keeps its high mechanical strength when using moulding sands with higher temperatures. Applications
Properties
|
| General Information | |
|---|---|
| Features |
|
| Appearance |
|
| Processing Method |
|
| Hardness | Nominal Value | Test Method | |
|---|---|---|---|
| Shore Hardness (Shore D) | 87 to 93 | ISO 7619 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flexural Modulus | 6200 to 7200 | MPa | ISO 178 |
| Flexural Stress | 63.0 to 73.0 | MPa | ISO 178 |
| Compressive Stress | 80.0 to 90.0 | MPa | ISO 604 |
| Taber Abrasion Resistance (250 Cycles, 500 g, H-18 Wheel) | 125 | mg | Internal Method |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Unnotched Impact Strength | 5.0 to 6.0 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (0.45 MPa, Unannealed) | 77.0 to 83.0 | °C | ISO 75-2/B |
| Thermoset | Nominal Value | Unit | |
|---|---|---|---|
| Thermoset Components | |||
| Hardener | Mix Ratio by Weight: 25 | ||
| Resin | Mix Ratio by Weight: 100 |
| Uncured Properties | Nominal Value | Unit | |
|---|---|---|---|
| Density (20°C) | 1.60 to 1.70 | g/cm³ | |
| Viscosity (25°C) | 3.7 to 5.3 | Pa·s | |
| Curing Time (20°C) | 8.0 to 12 | hr | |
| Pot Life 1(20°C) | 25 to 35 | min |
| Note Message | |
|---|---|
| 1 . | 200 g |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Radilon® A HSX 100 NAT | Radici Plastics | Nylon 66 | Radilon® |
| Ultramid® B3WGM24 sw23228 | BASF Corporation | Nylon 6 | Ultramid® |
| FRIANYL® B3 GF30 V0XI | Nilit Plastics | Nylon 6 | FRIANYL® |
| Latigloss 66 H2 G/50 | LATI S.p.A. | Nylon 66 | Latigloss |
| Pearlbond™ 104 | Lubrizol Advanced Materials, Inc. | TPU, Unspecified | Pearlbond™ |