Alathon® M6580
| Category: | HDPE , High Density Polyethylene |
| Manufacturer: | LyondellBasell Industries |
| Trademark: | Alathon® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Z3IB5d_Alathon-M6580.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| ALATHON M6580 is a narrow molecular weight distribution homopolymer that enhances processibility and stiffness, exhibits excellent color, low odor and good processing stability. Typical applications include cases, crates, trays, tote bins, ATV parts and open-head pails. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.965 | g/cm³ | ASTM D1505 |
| Apparent Density | 0.53 to 0.59 | g/cm³ | ASTM D1895 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 8.2 | g/10 min | ASTM D1238 |
| Spiral Flow | 25.1 | cm | Internal Method |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 73 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | ASTM D638 | ||
| -- 1 | 1240 | MPa | |
| 1% Secant | 932 | MPa | |
| Tensile Strength 2 | ASTM D638 | ||
| Yield | 32.1 | MPa | |
| Break | 31.0 | MPa | |
| Tensile Elongation 3 | ASTM D638 | ||
| Yield | 7.0 | % | |
| Break | 16 | % | |
| Flexural Modulus 4 | ASTM D790 | ||
| 1% Secant | 1650 | MPa | |
| 2% Secant | 1400 | MPa |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 36 | J/m | ASTM D256 |
| Unnotched Izod Impact | No Break | ASTM D4812 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed) | 82.8 | °C | ASTM D648 |
| Brittleness Temperature | -72.8 | °C | ASTM D746 |
| Vicat Softening Temperature | 131 | °C | ASTM D1525 |
| Peak Melting Temperature | 133 | °C | ASTM D3418 |
| Peak Crystallization Temperature (DSC) | 118 | °C | ASTM D3418 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Rear Temperature | 232 | °C | |
| Middle Temperature | 243 | °C | |
| Front Temperature | 246 | °C | |
| Nozzle Temperature | 246 | °C |
| Note Message | |
|---|---|
| 1 . | Type I, 50 mm/min |
| 2 . | Type IV, 50 mm/min |
| 3 . | Type IV, 50 mm/min |
| 4 . | 13 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Devcon Titanium Putty | Devcon | Epoxy | Devcon |
| HIVAL® 521054 | Nexeo Solutions, LLC. | HDPE | HIVAL® |
| InnoPlus HD8200B | PTT Global Chemical Public Company Limited | HDPE | InnoPlus |
| WELLAMID Nylon 6600/58 GV 30 HWUVCP | CP-Polymer-Technik GmbH & Co. KG | Nylon 66 | WELLAMID Nylon |
| Sylvin 9302-70 FUV WHITE 1337 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |