Lucon® CP6062EX
| Category: | PC+ABS , Polycarbonate + ABS |
| Manufacturer: | LG Chem Ltd. |
| Trademark: | Lucon® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Z31vNQ_Lucon-CP6062EX.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Lucon® CP-6062EX is a Polycarbonate + ABS (PC+ABS) material filled with carbon nano. It is available in Asia Pacific, Europe, Latin America, or North America for injection molding or sheet extrusion. Important attributes of Lucon® CP-6062EX are:
Typical application of Lucon® CP-6062EX: Sheet |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.21 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (300°C/2.16 kg) | 20 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (3.20 mm) | 0.50 to 0.70 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Yield, 3.20 mm) | 58.8 | MPa | ASTM D638 |
| Tensile Elongation 2(Break, 3.20 mm) | 14 | % | ASTM D638 |
| Flexural Modulus 3(3.20 mm) | 2750 | MPa | ASTM D790 |
| Flexural Strength 4(3.20 mm) | 98.1 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.20 mm) | 34 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed, 6.40 mm) | 110 | °C | ASTM D648 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+4 to 1.0E+6 | ohms | IEC 60093 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 70.0 to 80.0 | °C | |
| Drying Time | 5.0 to 7.0 | hr | |
| Rear Temperature | 280 to 300 | °C | |
| Middle Temperature | 290 to 310 | °C | |
| Front Temperature | 290 to 310 | °C | |
| Nozzle Temperature | 290 to 310 | °C | |
| Processing (Melt) Temp | 290 to 310 | °C | |
| Mold Temperature | 60.0 to 80.0 | °C | |
| Back Pressure | 0.00 to 0.981 | MPa | |
| Screw Speed | 40 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| 3 . | 15 mm/min |
| 4 . | 15 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Borealis PP QB341 | Borealis AG | PP, Unspecified | Borealis PP |
| ENFLEX VU-120-45A | ENPLAST, a Ravago Group Company | TPV | ENFLEX |
| HiFill® PP CO GF20 CC | Techmer Engineered Solutions | PP Copolymer | HiFill® |
| KOPLA PA6 KNX1067 | KOPLA Co., Ltd. | Nylon 6 | KOPLA PA6 |
| Medalist® MD-53293 (PRELIMINARY DATA) | Teknor Apex Company | TPE | Medalist™ |